Oligomerization of cadmium chalcogenide nanocrystals into CdTe-containing superlattice chains.
نویسندگان
چکیده
Hierarchically-assembled binary cadmium chalcogenide (CdX, X = S, Se, Te) oligomers were engineered. CdTe precursor injections into a solution containing seeded nanocrystals provided longer oligomers possessing alternating and phase-separated CdX and CdTe constituents in the same wire, like an alternating copolymer.
منابع مشابه
CdTe Quantum Dot Fluorescence Modulation by Spin Crossover
Nanocomposite materials containing Cadmium Telluride (CdTe) nanocrystals and [Fe(H-trz)2(trz)]BF4 nanoparticles were synthesized and investigated for the coupling between their photoluminescent and spin crossover properties. The bright CdTe emission around 550 nm was found to decrease reversibly when switching the ferrous complex from the high spin (HS) to the low spin (LS) state, which was att...
متن کاملOptical and structural characterization of oleic acid-stabilized CdTe nanocrystals for solution thin film processing
This work presents results of the optical and structural characterization of oleic acid-stabilized cadmium telluride nanocrystals (CdTe-NC) synthesized by an organometallic route. After being cleaned, the CdTe-NC were dispersed in toluene to obtain an ink-like dispersion, which was drop-cast on glass substrate to deposit a thin film. The CdTe-NC colloidal dispersion as well as the CdTe drop-cas...
متن کاملElectron-Transport and Cyclotron-Resonance in [211]-Oriented HgTe-CdTe Superlattices
We discuss a magneto transport and magneto-optical investigation of [211 ]-oriented HgTe-CdTe superlattices. Measurements were performed on seven n-type samples with well widths in the range 41-125 A and energy gaps between 0 and 128 meV. Both magnetotransport and magneto-optical results give evidence for an additional electron species besides the superlattice electrons and holes usually observ...
متن کاملColloidal synthesis and optical properties of type-II CdSe-CdTe and inverted CdTe-CdSe core-wing heteronanoplatelets.
We developed colloidal synthesis to investigate the structural and electronic properties of CdSe-CdTe and inverted CdTe-CdSe heteronanoplatelets and experimentally demonstrate that the overgrowth of cadmium selenide or cadmium telluride core nanoplatelets with counterpartner chalcogenide wings leads to type-II heteronanoplatelets with emission energies defined by the bandgaps of the CdSe and Cd...
متن کاملLuminescence Properties of Thiol-Stabilized CdTe Nanocrystals
Thiol-capped CdTe nanocrystals with cubic zinc blende structure are synthesized in aqueous solution. Their steady-state and time-resolved luminescence characteristics are studied at room and liquid nitrogen temperatures. A strong exciton luminescence peak at 2.3 eV dominates the emission spectrum of CdTe nanocrystals at room temperature, whereas the trap band centered at 2.0 eV undergoes substa...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 47 40 شماره
صفحات -
تاریخ انتشار 2011