Characterization of ultrathin InSb nanocrystals film deposited on SiO2/Si substrate

نویسندگان

  • Dengyue Li
  • Hongtao Li
  • Hehui Sun
  • Liancheng Zhao
چکیده

Recently, solid-phase recrystallization of ultrathin indium antimonide nanocrystals (InSb NCs (films grown on SiO2/Si substrate is very attractive, because of the rapid development of thermal annealing technique. In this study, the recrystallization behavior of 35 nm indium antimonide film was studied. Through X-ray diffraction (XRD) analysis, it is demonstrated that the InSb film is composed of nanocrystals after high temperature rapid thermal annealing. Scanning electron microscopy shows that the film has a smooth surface and is composed of tightly packed spherical grains, the average grain size is about 12.3 nm according to XRD results. The optical bandgap of the InSb NCs film analyzed by Fourier Transform infrared spectroscopy measurement is around 0.26 eV. According to the current-voltage characteristics of the InSb NCs/SiO2/p-Si heterojunction, the film has the rectifying behavior and the turn-on voltage value is near 1 V.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Photoemission measurements of Ultrathin SiO2 film at low take-off angles

The surface and interfacial analysis of silicon oxide film on silicon substrate is particularly crucial in the nano-electronic devices. For this purpose, series of experiments have been demonstrated to grow oxide film on Si (111) substrate. Then these films have been used to study the structure of the film by using X-ray photo emission spectroscopy (XPS) technique. The obtained results indicate...

متن کامل

TEM study on the evolution of Ge nanocrystals in Si oxide matrix as a function of Ge concentration and the Si reduction process

Growth and evolution of germanium (Ge) nanocrystals embedded into a silicon oxide (SiO2) system have been studied based on the Ge content of co-sputtered Ge-SiO2 films using transmission electron microscopy (TEM) and Xray photoelectron spectroscopy (XPS). It was found that when the proportion of Ge relative to Ge oxide is 20%, TEM showed that annealing the samples at 800C for 60 min resulted in...

متن کامل

Parametric study on electrochemical deposition of copper nanoparticles on an ultrathin polypyrrole film deposited on a gold film electrode.

Monoshaped and monosized copper nanostructured particles have been prepared by potentiostatic electrochemical deposition on an ultrathin polypyrrole (PPY) film, electrochemically grown on a Si(100) substrate sputter-coated with a thin gold film or gold-film electrode (GFE). The crystal size and the number density of the copper nanocrystals have been examined by varying several deposition parame...

متن کامل

Fabrication of MgF2-SiO2 Nanocomposite Thin Films and Investigation of Their Optical and Hydrophobic Properties

In this research, MgF2-2%SiO2/MgF2 thin films were applied on a glass substrate. At first, MgF2 thin films with the optical thickness were deposited on the glass slide substrates. Then, MgF2-2%SiO2 thin films were deposited on the glass coated with MgF2 thin films. Finally, the nanocomposite thin films were surface treated by the PFTS solution. Characterization of the thin film was done by X-Ra...

متن کامل

Depth distribution of luminescent Si nanocrystals in Si implanted SiO2 films on Si

Depth-resolved measurements of the photoluminescence of Si implanted and annealed SiO2 films on Si have been performed to determine the depth distribution of luminescent Si nanocrystals. Si nanocrystals with diameters ranging from ;2 to 5 nm were formed by implantation of 35 keV Si ions into a 110-nm-thick thermally grown SiO2 film on Si~100! at a fluence of 6310 16 Si/cm, followed by a thermal...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 6  شماره 

صفحات  -

تاریخ انتشار 2011