Experimental Parametric Model for Indirect Adhesion Wear Measurement in the Dry Turning of UNS A97075 (Al-Zn) Alloy
نویسندگان
چکیده
In this work, the study of the influence of cutting parameters (cutting speed, feed, and depth of cut) on the tool wear used in in the dry turning of cylindrical bars of the UNS A97075 (Al-Zn) alloy, has been analyzed. In addition, a study of the physicochemical mechanisms of the secondary adhesion wear has been carried out. The behavior of this alloy, from the point of view of tool wear, has been compared to similar aeronautical aluminum alloys, such as the UNS A92024 (Al-Cu) alloy and UNS A97050 (Al-Zn) alloy. Furthermore, a first approach to the measurement of the 2D surface of the adhered material on the rake face of the tool has been conducted. Finally, a parametric model has been developed from the experimental results. This model allows predicting the intensity of the secondary adhesion wear as a function of the cutting parameters applied.
منابع مشابه
Machinability Improvement of 17-4PH Stainless Steel by Cryogenic Cooling
17-4PH stainless steel is a martensitic precipitation hardening stainless steel that provides an outstanding combination of high strength, good corrosion resistance, good mechanical properties, good toughness in both base metal and welds, and short time, low-temperature heat treatments that minimize warpage and scaling. This valuable alloy is widely used in the aerospace, nuclear, chemical, pet...
متن کاملMachinability Improvement of 17-4PH Stainless Steel by Cryogenic Cooling
17-4PH stainless steel is a martensitic precipitation hardening stainless steel that provides an outstanding combination of high strength, good corrosion resistance, good mechanical properties, good toughness in both base metal and welds, and short time, low-temperature heat treatments that minimize warpage and scaling. This valuable alloy is widely used in the aerospace, nuclear, chemical, pet...
متن کاملEFFECTS OF Al-5TI-1B MASTER ALLOY AND HEAT TREATMENT ON THE MICROSTRUCTURE AND DRY SLIDING WEAR BEHAVIOR OF AN Al-12Zn-3Mg-2.5Cu ALLOY
In this study the effect of Al–5Ti–1B grain refiner on the structural characteristics and wear properties of Al–12Zn–3Mg–2.5Cu alloy was investigated. The optimum amount for Ti containing grain refiners was selected as 2 wt.%. T6 heat treatment, (i.e. heating at 460 °C for 1 h before water quenching to room temperature and then aging at 120 °C for 24 h) was applied for all specimens before wear...
متن کاملFabrication of the Cu-Zn multilayer and Cu-Zn alloy by accumulative roll bonding (ARB) with an emphasis on the wear behavior
Accumulative roll bonding (ARB) was used to fabricate the Cu-Zn multilayer and Cu-Zn solid solution. A lamellar structure with the hardness of about 130 VHN was formed after eight ARB cycles. Following to the suitable heat treatment, a solid solution with a uniform microstructure and hardness of about 57 VHN was produced. The dominant wear mechanism in the ARB processed multilayer was found to ...
متن کاملEnhancing Wear Resistance of Squeeze Cast AC2A Aluminum Alloy
The effect of squeeze casting process parameters on wear behavior of AC2A aluminium alloy was primarily investigated in this experimental study. Five process parameters, namely squeeze pressure, pouring temperature, die temperature, die material and compression time, each at four levels were chosen and sixteen experimental runs based on L16 orthogonal array were performed. From analysis of vari...