Achievement of Diverse Domain Structures in Soft Magnetic Thin Film through Adjusting Intrinsic Magnetocrystalline Anisotropy

Oriented soft magnetic hcp-Co1 - x Ir x films with a fixed thickness of 120 nm were fabricated. All prepared films exhibit soft magnetic properties but various magnetocrystalline anisotropies with the variation of Ir content. The measured data shows that diverse domain structures including the Néel wall, Bloch wall, and stripe domains present in a fixed film thickness. It is singular for the single-layer soft magnetic film to possess diverse domains in a fixed thickness. This phenomenon was explained by introducing intrinsic magnetocrystalline anisotropy energy into soft magnetic films rather than the structural parameters of the film, inner stress, and microstructure effect.