Effect of refrigeration on bond strength of self-etching adhesive systems.
نویسندگان
چکیده
The purpose of this study was to investigate the tensile bond strength to dentin of three self-etching adhesive systems at refrigerated and room temperatures. Seventy-eight bovine incisors were embedded in self-cured acrylic resin, abraded on a water-cooled lathe and polished with 400- and 600-grit sandpapers to obtain standard dentin surfaces. The specimens were randomly assigned to 6 groups (n=13). Clearfil SE Bond, AdheSE and One-Up Bond F adhesive systems at refrigerated (4 degrees C) and room temperatures (23 degrees C) were applied to dentin according to the manufacturers' instructions. A truncated composite resin (Herculite XRV) cone was bonded to dentin surface. The specimens were stored in distilled water at 37 degrees C for 24 h and submitted to tensile bond strength testing at a crosshead speed of 0.5 mm/min. Means in MPa were analyzed statistically by Student's t-test at 5% significance level. No statistically significant differences (p>0.05) were found between the adhesive systems applied at refrigerated and room temperatures. In conclusion, no adverse effects on tensile bond strength were observed when self-etching adhesive systems were used after being taken directly from the refrigerated storage.
منابع مشابه
Effect of Saliva Contamination and sequencing time of curing the Transbond™ Plus Self Etching Primer on the Shear Bond Strength of Orthodontic Brackets
Abstract Background and aim: Over the years, improvments have been done to simplify clinical bonding procedure. One of these material is Transbond™ Plus Self Etching. The aim of this study was to evaluate the effect of saliva contamination and reusing Transbond™ Plus Self Etching Primer (SEP) on shear bond strength of orthodontic brackets. Materials and Methods: Fifty premolars divided into fiv...
متن کاملComparison of Shear Bond Strength of Composite Restorations to Intact Enamel of Primary Incisors When Using Different Conditioners and Adhesive Systems
Introdouction: Esthetic demands of patients have led to the introduction of tooth-colored restorations wherecomposite resins are bonded to the enamel using acid etch techniques. Total etch adhesion systems are still considered as the gold standard among bonding systems. However, clinicians have a tendency to use adhesive systems with simpler application procedures. The aim of the present stu...
متن کاملEffect of Chlorhexidine on Micro-Shear Bond Strength of Two Adhesive Systems After Aging
Background and Aim: Recurrent caries and low bond strength are the main causes of composite restorations failure. This study sought to assess the effect of chlorhexidine (CHX) on micro-shear bond strength (MSBS) to dentin of a fourth generation adhesive system and a universal bonding agent after aging. Materials and Methods: This in vitro study used 32 extracted third molars and 3-5mm thick de...
متن کاملIn vitro study of the effect of sodium hypochlorite and type of bonding on the shear bond strength of the composite to the bovine dentin
In vitro study of the effect of sodium hypochlorite and type of bonding on the shear bond strength of the composite to the bovine dentinDr. Kermanshah, H.* - Dr. Ghanbaripour H.** *Assistant Professor of Operative Dentistry Dept., Faculty of Dentistry, Tehran University / Medical Sciences. **Dentist. Abstract Background & Aim: Recent studies have reported the increase in bonding stability whe...
متن کاملمقایسه سه سیستم self-etch adhesive در استحکام برشی باند کامپوزیتبه مینا در شرایط خشک و مرطوب
Background and Aim: The bonding mechanisms of self etching primers, based upon the simultaneous etching and priming of dentin, simplifies the bonding technique, but the efficiency of these systems is still controversial. This study compared the shear bond strength of three self etch adhesive systems in dry and wet conditions. Materials and Method: In this experimental study, 77 intact bovine lo...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Brazilian dental journal
دوره 17 3 شماره
صفحات -
تاریخ انتشار 2006