Acrylic coatings with surprising antifogging and frost-resisting properties.
نویسندگان
چکیده
We report an unusually effective antifogging/frost-resisting coating based on conventional acrylic polymers. The intriguing antifogging property originated from the delicate balance between the hydrophilicity and hydrophobicity of the acrylic copolymers of 2-(dimethylamino)ethyl methacrylate and methyl methacrylate, as well as between the water-swellability of the copolymer and the cross-linked network due to ethylene glycol dimethacrylate.
منابع مشابه
Improved Fastness Properties of some Novel Triarylmethane Dyes on Acrylic Fibres
In this research, several series of triarylmethane dyes containing one or more terminal methoxy substituents with a variable tertiary amino groups have been used. These dyes have been applied to different substrates by using various methods including transfer printing and then their fastness properties were measured. These dyes shows exceptionally high light fastness (6-7) on acid modified poly...
متن کاملAcrylic resin derivatives as modifier for potassium silicate binder in zinc-rich coatings: electrochemical studies
Water based inorganic alkali silicate binder of zinc rich primer was modified by adding acrylic resin derivatives. Several series of primer coatings were formulated by adding 5, 10 and 15 wt of acrylic and acrylic/styrene copolymer to potassium silicate binder and used as binder in zinc rich coatings. The formulated primers were applied on low carbon steel plates and the corrosion protection pr...
متن کاملNanocomposite Coating Based on Thermoplastic Acrylic Resin and Montmorillonite Clay: Preparation and Corrosion Prevention Properties
Different amounts of nanoclay were incorporated into the acrylic resin matrix at 0, 1, 3, and 5 wt.% loadings. The coatings were applied on low carbon steel plates. Optical microscopy, sedimentation test, transmission electron microscopy, and X-ray diffraction were employed to investigate the dispersion of nanoclay in matrix. The corrosion resistance of coatings was evaluated by electrochemical...
متن کاملStudy the curing behavior and mechanical properties of Pigmented UV curable epoxy acrylate monomers
The formulations contained different acrylate monomer with different structure and functionalities and TiO2, were applied to obtain pigmented acrylic films by UV exposure. The conversion and mechanical characteristic were correlated. The results showed that there is a significant interaction between pigment, reactive diluents’ type and mechanical properties of coatings. It seems that cured film...
متن کاملIR-reflective Opaque Water-based Acrylic Coatings on White Pine Wood Substrates
Two sets of opaque water-based acrylic coatings were prepared with IR-reflective pigments and conventional pigments. The objective of this work was to determine the efficiency of IR-reflective pigments in limiting the heat buildup of opaque coating formulations. Experiments performed on PVC substrates revealed that IR-reflective pigments significantly decreased the temperature increase above ro...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 49 100 شماره
صفحات -
تاریخ انتشار 2013