Excess Heat and Unexpected Elements from Electrolysis of Heavy Water with Titanium Cathodes
نویسندگان
چکیده
Excess heat was produced at the rate of about 1.2 watts during electrolysis of heavy water with a titanium cathode weighing 0.0625 g. Analysis of the electrodes before and after electrolysis with a scanning electron microscope (SEM) and an energy dispersive spectrometer (EDS) revealed that new surface topographical features with concentrations of unexpected elements (S, K, Ca, V, Cr, Fe, Ni, and Zn ) formed during electrolysis.
منابع مشابه
Excess Heat and Unexpected Elements from Aqueous Electrolysis with Titanium and Palladium Cathodes
Presented here are results of research performed at Portland State University during the period 1994 to 1996. Excess heat was produced at the rate of about 1.2 watts during electrolysis of heavy water with a titanium cathode weighing 0.0625g. Analysis of the electrodes before and after electrolysis with a scanning electron microscopy (SEM) and an energy dispersive spectrometer (EDS) revealed th...
متن کاملEXCESS HEAT REPRODUCIBILITY AND EVIDENCE OF ANOMALOUS ELEMENTS AFTER ELECTROLYSIS IN Pd|D2O+H2SO4 ELECTROLYTIC CELLS
Electrolyte temperature is a key factor in excess heat production using Pd|D2O+H2SO4 electrolytic cells. Best results are obtained when the electrolyte temperature is close to the boiling point. Stable excess heat is generated by events on or near the Pd cathode surface. In addition to the stable excess heat, heat bursts are sometimes observed. These occurred most frequently in experiments usin...
متن کاملElectrochemical Calorimetric Studies of the Cold Fusion Effect
Several types of calorimetric cell designs were used in attempts to measure excess enthalpy during the electrolysis of LiOD/D2O using palladium cathodes. Control experiments were run by using light water in place of D2O or by using platinum cathodes in place of palladium. Initial experiments using thin palladium cathodes of an unknown purity gave no significant differences between the Pd/D2O ce...
متن کاملHEAT MEASUREMENT DURING LIGHT WATER ELECTROLYSIS USING Pd/Ni ROD CATHODES
The heat balance under electrolysis in 1M Li2SO4 light water solutions was measured using Pd rods or Pd coated Ni (Pd/Ni) rods for cathode. We detected large excess heat of more than 10% in 6 of 28 experiments. However, in many other experiments, no excess or only small excess heat was observed. In most cases the excess heat was 5% or less. In order to confirm the excess heat, we have to find t...
متن کاملCALORIMETRIC MEASUREMENTS DURING Pd-Ni THIN FILM– CATHODES ELECTROLYSIS IN Li2SO4/H2O SOLUTION
A sensitive open-type calorimeter was used to measure excess heat production during electrolysis in Li2SO4/H2O solution with Pt-anode and Pd-Ni thin film cathodes 9000 Å thick, sputtered on Al2O3 substrate. In order to estimate the actual performance and possible measurement errors during electrolysis in the calorimeter used, including heat convection, bubbling and possible H2+O2 recombination,...