Magnetic properties and structure of Fe/Pt thin films
The structural transfqmation from fcc to fct and relevant magnetic properties of initially multilayered Fe/Pt films were studied. When the asdeposited FePt films were annealed at the temperature of 300°C and up, the fct-phase was formed. Rather square hysteresis loops and large coercivities were measured from the annealed films. The films annealed at 300°C retain a layered structure.
متن کاملPermanent-Magnet Properties of Thermally Processed FePt and FePtâ•fiFe Multilayer Films
FePt single-layer and FePt–Fe multilayer thin films are prepared by magnetron sputtering. By varying the Pt content, FePt, Fe3Pt, or a mixture of FePt and Fe3Pt can be obtained in Fe–Pt single layers. In annealed FePt–Fe multilayers, the coercivities decrease with the introduction of Fe layers compared to FePt single layers, while the magnetization increases. The single-phase behavior of the hy...
متن کاملHydrothermal Synthesis of Ultrasmall Pt Nanoparticles as Highly Active Electrocatalysts for Methanol Oxidation
Ultrasmall nanoparticles, with sizes in the 1-3 nm range, exhibit unique properties distinct from those of free molecules and larger-sized nanoparticles. Demonstrating that the hydrothermal method can serve as a facile method for the synthesis of platinum nanoparticles, we successfully synthesized ultrasmall Pt nanoparticles with an average size of 2.45 nm, with the aid of poly(vinyl pyrrolidon...
متن کاملSuperparamagnetic Behavior of the Magnetic Hysteresis Loop in the Fe2O3@Pt Core-Shell Nanoparticles
Studies of the magnetization of Fe2O3@Pt nanoparticles at room temperature showed that there is superparamagnetic contribution with high saturation magnetization about 12.35(emu/g), and soft ferromagnetic contribution with narrow coercive field about 58(Oe). In this paper we fitted the hystersis loop of sample with Brillouin function that demonstrating existence of superparamagnetic phase. Tota...
متن کاملStructural and Magnetic Investigations on FePt Nanoparticles
Magnetic nanoparticles and thin films exhibiting a large magnetic anisotropy energy density (MAE) have attracted enormous attention over the last years due to their potential use in magnetic data storage or sensing applications. FePt alloy nanoparticles and films have a huge MAE in the chemically ordered L10 phase. This ordered phase is typically obtained by annealing the as-prepared chemically...