Growth of thin alumina films on a vicinal NiAl surface
نویسندگان
چکیده
Dramatic changes in the surface morphology have been observed during the oxidation of stepped NiAl(16,14,1) by LEED and STM. The initial sequence of identical (110) terraces is lifted in favor of large, triangular planes, whose mean size is determined by the mismatch-induced stress that accumulates in the thin alumina film. The asymmetry of the original step direction on NiAl(16,14,1) with respect to the orientation of the two alumina reflection domains favors the formation of one domain type, for which the stress relief via NiAl step edges is particularly efficient.
منابع مشابه
Substrate Effects on the Structural Properties of Thin Films of Lead Sulfide
Nanocrystalline PbS thin films are deposited on glass and alumina substratesthrough the chemical bath deposition technique by creating similar conditions, in orderto investigate the effects of the substrate. The structural and optical properties of PbSfilms are investigated by X-ray diffraction, scanning electron microscope, and UV–Vis.The structural analyses of the films indicate that they are...
متن کاملStructural Dynamics of Al2O3/NiAl(110) During Film Growth in NO2
While continuum descriptions of oxide film growth are well established, the local structural dynamics during oxide growth are largely unexplored. Here, we investigate this using scanning tunneling microscopy (STM) and X-ray photoelectron spectroscopy (XPS) for the example of alumina film growth on NiAl(110) following NO2 exposure. To maintain a well-defined system, we have adopted a cyclic grow...
متن کاملInteraction of oxygen with chromium deposited on Al2O3/NiAl(1 1 0)
We have investigated the growth and reactivity of chromium layers deposited onto a thin alumina film at room temperature and at 570 K. The interaction between Cr and the Al2O3/NiAl(1 1 0) surface leads to partial oxidation to Cr2þ and Cr3þ species. Complete oxidation to Cr3þ was achieved using moderate O2 doses at room temperature in vacuum. Cr has also been deposited in an O2 background pressu...
متن کاملEffect of Thickness on Properties of Copper Thin Films Growth on Glass by DC Planar Magnetron Sputtering
Copper thin films with nano-scale structure have numerous applications in modern technology. In this work, Cu thin films with different thicknesses from 50–220 nm have been deposited on glass substrate by DC magnetron sputtering technique at room temperature in pure Ar gas. The sputtering time was considered in 4, 8, 12 and 16 min, respectively. The thickness effect on the structural, mo...
متن کاملSurface step terrace tuned microstructures and dielectric properties of highly epitaxial CaCu3Ti4O12 thin films on vicinal LaAlO3 substrates
Controllable interfacial strain can manipulate the physical properties of epitaxial films and help understand the physical nature of the correlation between the properties and the atomic microstructures. By using a proper design of vicinal single-crystal substrate, the interface strain in epitaxial thin films can be well controlled by adjusting the miscut angle via a surface-step-terrace matchi...
متن کامل