Effect of Resin Cement Pre-heating on the Push-out Bond Strength of Fiber Post to Root Canal Dentin
نویسندگان
چکیده
Background and aims. Various factors influence the interfacial bond between the fiber posts and root canal dentin. The aim of the present study was to evaluate the effect of pre-warming of resin cement on the push-out bond strength of fiber posts to various segments of root canal dentin. Materials and methods. In this in vitro study, 40 single-rooted human premolars were decoronated and underwent root canal treatment along with post space preparation. The samples were randomly divided into two groups: In group 1, Panavia F 2.0 cement was used at room temperature; in group 2, the same cement was warmed to 55‒60°C before mixing. After fiber posts were placed and cemented in the root canals, 3 dentin/post sections (coronal, middle and apical) with a thickness of 3 mm were prepared. A universal testing machine was used to measure push-out bond strength in MPa. Data was analyzed using two-factor ANOVA and a post hoc Tukey test at α=0.05. Results. The mean value of push-out bond strength was high at room temperature, and the differences in the means of push-out bond strength values between the resin cement temperatures and between different root segments in each temperature were significant (P<0.05). Conclusion. Pre-warming of Panavia F 2.0 resin cement up to 55‒60°C reduced push-out bond strength to root canal dentin. In addition, in each temperature group bond strengths decreased from coronal to apical segments.
منابع مشابه
Effect of Resin Cement Pre-heating on the Push-out Bond Strength of Fiber Post to Root Canal Dentin
Background and aims. Various factors influence the interfacial bond between the fiber posts and root canal dentin. The aim of the present study was to evaluate the effect of pre-warming of resin cement on the push-out bond strength of fiber posts to various segments of root canal dentin. Materials and methods . In this in vitro study, 40 single-rooted human premolars were decoronated and underw...
متن کاملبررسی مقایسهای استحکام باند پست فایبر به در مقاطع مختلف عاج ریشه با سه نوع سمان رزینی (Rebilda, BifixQM, BifixSE)
Background and Aims: In endodontically treated teeth, the fiber posts are used to retain a core restoration. The purpose of this study was to evaluate the effect of different resin cements on the bond strength of fiber reinforced composite posts to root canal dentin, and comparing the bond strength in different sections of root. Materials and Methods: In this in-vitro experimental study, 48 ex...
متن کاملThe Effect of Resin Cement Type and Cementation Technique on Bond Strength of Fiber Posts
Background: Resin cements are widely used for cementation of FRC posts, but their bond strength can be influenced by cement type and cementation technique. The aim of this study was to determine the effect of type of resin cement and cementation technique on the bond strength of fiber posts. Methods: Forty five extracted mandibular premolars with a minimum roo...
متن کاملEffect of various intracanal medicaments on the bond strength of self-adhesive resin cement to root canal dentin
Objective: It has been shown that the irrigating solutions and medicament used during root canal treatment may affect the bonding strength. The aim of this study was to evaluate the effect of triple antibiotic paste (TAP), double antibiotic paste (DAP) and calcium hydroxide (CH) on the bond strength to root dentin of self-adhesive resin cement. Materials and methods: Forty-eight single-rooted h...
متن کاملEffect of root canal rinsing protocol on dentin bond strength of two resin cements using three different method of test
BACKGROUND Different studies have used different tests to evaluate bond strength of resin cements to root dentin. In this in vitrostudy, three different tests were used to evaluate the bond strength of two resin cements to root dentin using two root dentin irrigation protocols. MATERIAL AND METHODS Ninety-six intact single-rooted teeth were selected for this study. Forty-eight teeth, with a r...
متن کامل