The Influence of Interface Characteristics on the Adhesion/Cohesion of Plasma Sprayed Tungsten Coatings

نویسندگان

  • Jiří Matějíček
  • Monika Vilémová
  • Radek Mušálek
چکیده

Tungsten is the prime candidate material for plasma facing components of future fusion devices. Plasma spraying, with its ability to coat large areas, including non-planar surfaces, with a significant thickness, is a prospective fabrication technology for components subject to moderate heat loads, e.g., the first wall of the Demonstration Reactor (DEMO). The functionality of such coatings is critically dependent on their adhesion to the underlying material. This in turn, is influenced by a variety of processing-related factors, chief among them being the state of the interface. In this study, the effects of two factors—surface roughness and the presence of thin interlayers—were investigated. Two different levels of roughness of steel substrates were induced by grit blasting, and two thin interlayers—titanium (Ti) and tungsten (W)—were applied by physical vapor deposition prior to plasma spraying of W by a Water Stabilized Plasma (WSP) torch. Coating adhesion was determined by a shear adhesion test. The structures of the coatings and the interfaces, as well as the characteristics of the fractured surfaces, were observed by SEM.

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Effect of morphology and nonbounded interface on dielectric properties of plasma sprayed BaTiO3 Coating

In this research, BaTiO3 thick deposit has been successfully sprayed by air plasma spray. The microstructure and dielectric properties of thick films were investigated by secondary electron microscopy (SEM) and LCR meter respectively. XRD measurement was carried out on plasma sprayed BaTiO3. The results illustrate differences in the crystal structure between plasma sprayed coatings and feed sto...

متن کامل

Air Plasma Sprayed Bond Coat Oxidation Behavior and its Resistance to Isothermal and Thermal Shock Loading

An experimental investigation was conducted to find the effect of spraying method of coating of Thermal Barrier Coatings (TBCs) on their oxidation behaviour and resistance to various thermal loading. Isothermal and thermal shock tests were performed in order to study oxidation behaviour of air plasma sprayed Bond Coat (BC) and assess its effect on TBCs lifetime under the stated loadings. Specim...

متن کامل

Analytically Modeling of In Vitro Calcium Dissolution of Plasma- Sprayed Hydroxyapatite Coatings

      The in vitro dissolution of plasma-sprayed hydroxyapatite (PHA) coatings with different characteristics, produced by various spraying conditions, in a Tris-buffered solution at pH 7.4 was experimentally studied through the measurement of calcium ions release with Inductively Coupled Plasma Atomic Emission Spectroscopy (ICP-AES), and then modeled. Three coating characteristics, th...

متن کامل

Effect of Surface Roughness Morphology on Bond Strength of Thermal Sprayed WC-10Co-4Cr Ceramic/Metal Coating

In this study, the effect of surface roughness and roughness morphology on the bond strength of WC-Co-Cr coatings has investigated. The three different surfaces morphology are use for this purpose. The first and tow samples sandblasted with alumina and silicon carbide respectively. Other sample no sandblasted before spraying process. The same WC-10Co-4Cr coating deposited on the substrates with...

متن کامل

Influence of Electrolyte Composition and Voltage on the Microstructure and Growth Mechanism of Plasma Electrolytic Oxidation (PEO) Coatings on Tantalum: A Review

Recently, PEO process of tantalum has been developed as a method of producing corrosion-resistant, hard, wear-resistant, and biocompatible as well as having good adhesion coatings. In this review, we present the results of PEO process of tantalum in three main electrolytes. This review tries to measure the effect of electrolyte composition and voltage that were used within PEO procedure on the ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2013