On oscillatory microstructure during cellular growth of directionally solidified Sn–36at.%Ni peritectic alloy
نویسندگان
چکیده
An oscillatory microstructure has been observed during deep-cellular growth of directionally solidified Sn-36at.%Ni hyperperitectic alloy containing intermetallic compounds with narrow solubility range. This oscillatory microstructure with a dimension of tens of micrometers has been observed for the first time. The morphology of this wave-like oscillatory structure is similar to secondary dendrite arms, and can be observed only in some local positions of the sample. Through analysis such as successive sectioning of the sample, it can be concluded that this oscillatory microstructure is caused by oscillatory convection of the mushy zone during solidification. And the influence of convection on this oscillatory microstructure was characterized through comparison between experimental and calculations results on the wavelength. Besides, the change in morphology of this oscillatory microstructure has been proved to be caused by peritectic transformation during solidification. Furthermore, the melt concentration increases continuously during solidification of intermetallic compounds with narrow solubility range, which helps formation of this oscillatory microstructure.
منابع مشابه
Detachment of secondary dendrite arm in a directionally solidified Sn-Ni peritectic alloy under deceleration growth condition
In order to better understand the detachment mechanism of secondary dendrite arm during peritectic solidification, the detachment of secondary dendrite arm from the primary dendrite arms in directionally solidified Sn-36at.%Ni peritectic alloys is investigated at different deceleration rates. Extensive detachment of secondary dendrite arms from primary stem is observed below peritectic reaction...
متن کاملEffect of a weak transverse magnetic field on the microstructure in directionally solidified peritectic alloys
Effect of a weak transverse magnetic field on the microstructures in directionally solidified Fe-Ni and Pb-Bi peritectic alloys has been investigated experimentally. The results indicate that the magnetic field can induce the formation of banded and island-like structures and refine the primary phase in peritectic alloys. The above results are enhanced with increasing magnetic field. Furthermor...
متن کاملEvidence for the transition from primary to peritectic phase growth during solidification of undercooled Ni-Zr alloy levitated by electromagnetic field
The Ni83.25Zr16.75 peritectic alloy was undercooled by electromagnetic levitation method up to 198 K. The measured dendritic growth velocity shows a steep acceleration at a critical undercooling of ΔTcrit = 124 K, which provides an evidence of the transition of the primary growth mode from Ni7Zr2 phase to peritectic phase Ni5Zr. This is ascertained by combining the temperature-time profile and ...
متن کاملEffects of growth rate on the physical and mechanical properties of Sn-3.7Ag-0.9Zn eutectic alloy
Sn-3.7wt.%Ag-0.9wt.%Zn alloy was directionally solidified upward under different conditions, with different growth rates (V = 3.38 220.12 μm/s) at a constant temperature gradient (G = 4.33 K/mm) and with different temperature gradients (G = 4.33 -12.41 K/mm) at a constant growth rate (V = 11.52 μm/s) by using a Bridgman-type directional solidification furnace. The microstructure was observed to...
متن کاملStudy of Reactive Wetting of Sn–0.7Cu and Sn–0.3Ag–0.7Cu Lead Free Solders during Solidification on Nickel Coated Al Substrates
Microstructure, wetting behavior and interfacial reactions between Sn–0.7Cu and Sn–0.3Ag–0.7Cu (SAC0307) solders solidified on Ni coated Al substrates were compared and investigated. Microstructure of Sn–0.7Cu alloy exhibited a eutectic matrix composed of primary β-Sn dendrites with a fine dispersion of Cu6Sn5 intermetallics whereas microstructure of SAC0307 alloy exhibited coarser Cu6Sn5 and f...