A new method for the large-scale hydrothermal production and activation of ZIF-8 is presented in this communication. Activated ZIF-8 has been produced, at lab-scale and pilot-scale, at a rate of 27 g h(-1) and 810 g h(-1) respectively with the activated material showing a surface area of 1800 m(2) g(-1).
منابع مشابه
Improvement of hydrothermal stability of zeolitic imidazolate frameworks.
The metal-organic framework ZIF-8, which undergoes hydrolysis under hydrothermal conditions, is endowed with high water-resistance after a shell-ligand-exchange-reaction. The stabilized ZIF-8 retains its structural characteristics with improved application performances in adsorption and membrane separation.
متن کاملRapid synthesis of zeolitic imidazolate framework-8 (ZIF-8) nanocrystals in an aqueous system.
We report here the first example of ZIF materials synthesized in aqueous solution. The synthesis was performed at room temperature and typically took several minutes compared to hours and days in non-aqueous conditions. The obtained product were ZIF-8 nanocrystals having size of ~85 nm and showed excellent thermal, hydrothermal and solvothermal stabilities.
متن کاملAmorphization of the prototypical zeolitic imidazolate framework ZIF-8 by ball-milling.
We report the rapid amorphization of the prototypical substituted zeolitic imidazolate framework, ZIF-8, by ball-milling. The resultant amorphous ZIF-8 (a(m)ZIF-8) possesses a continuous random network (CRN) topology with a higher density and a lower porosity than its crystalline counterpart. A decrease in thermal stability upon amorphization is also evident.
متن کاملIn situ crystal growth of zeolitic imidazolate frameworks (ZIF) on electrospun polyurethane nanofibers.
This paper reports for the first time in situ crystal growth of ZIF-8 on electrospun polyurethane (PU) nanofibers. In SEM images, continuous and compact ZIF-8 nanocrystals grow along electrospun PU nanofibers. The highest loading capacity of ZIF-8 on PU reaches 63%. By N2 adsorption-desorption, ZIF-8-PU shows a high surface area of 566 cm(2) g(-1). Combining the good flexibility of PU with the ...
متن کاملExpression of Recombinant Factor IX Using the Transient Gene Expression Technique
Background: Pilot and large-scale production of recombinant proteins requires the presence of stable clones capable of producing large quantities of recombinant proteins. Not only the process of selecting stable clones is time consuming, but also the continuous culturing of clones in large-scale production may cause loss of incoming plasmid and recombinant genes. Thus, considering the advanceme...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 51 64 شماره
صفحات -
تاریخ انتشار 2015