Enhanced High Oxygen Permeation of Mixed-Conducting Multichannel Hollow Fiber Membrane via Surface Modified Porous Layer
نویسندگان
چکیده
The oxygen permeation performance of Ba0.5Sr0.5Co0.8Fe0.2O3−δ (BSCF) mixed-conducting multichannel hollow fiber (MCMHF) membranes was improved by surface modification via spin-spraying of a La0.6Sr0.4CoO3−δ (LSC) porous layer. At 1173 K, the oxygen permeation flux of the modified membranes was clearly enhanced and reached 9.68 mL·cm−2·min−1, which is a remarkable high value in the field of mixed-conducting oxygen permeation membrane processes. Theoretical calculations demonstrated that the oxygen transport resistance, especially the surface exchange resistance, obviously decreased as a result of the modified LSC porous layer. Moreover, the process of oxygen permeation through the modified membrane was controlled by both bulk diffusion and the surface oxygen exchange reaction, whereas the oxygen permeation of the unmodified membrane was dominantly controlled by the surface oxygen exchange reaction. The modified MCMHF membranes showed generally stable oxygen permeation fluxes over 100 h at 1173 K.
منابع مشابه
Multichannel Mixed-Conducting Hollow Fiber Membranes for Oxygen Separation
A multichannel mixed-conducting hollow fiber (MMCHF) membrane, 0.5 wt % Nb2O5-doped SrCo0.8 Fe0.2O3-d (SCFNb), has been successfully prepared by phase inversion and sintering technique. The crystalline structure, morphology, sintering behavior, breaking load, and oxygen permeability of the MMCHF membrane were studied systematically. The MMCHF membrane with porous-dense asymmetrical microstructu...
متن کاملCO2-tolerant mixed-conducting multichannel hollow fiber membrane for efficient oxygen separation
A mixed-conducting multichannel hollow fiber membrane (MCMHF) based on CO2-tolerant SrFe0.8Nb0.2O3–δ (SFN) oxide has been successfully prepared by phase inversion and sintering technique. The morphology, breaking load, oxygen permeability under CO2 atmosphere, thermal cycling performance and the long-term stability of the membrane were investigated in detail. The prepared membrane has a signifi...
متن کاملInfluence of permeation modes on oxygen permeability of the multichannel mixed-conducting hollow fibre membrane
A multichannel mixed-conducting hollow fibre (MMCHF) membrane, Ba0.5Sr0.5Co0.8Fe0.2O3 δ, has been successfully prepared by a combined phase inversion and sintering technique. Two possible permeation modes can be used in the hollow fibre membrane. One mode is that oxygen permeates from the shell side of the membrane to the lumen side (SL mode), with the other mode being in the direction from the...
متن کاملA Robust Mixed-Conducting Multichannel Hollow Fiber Membrane Reactor
To accelerate the commercial application of mixed-conducting membrane reactor for catalytic reaction processes, a robust mixed-conducting multichannel hollow fiber (MCMHF) membrane reactor was constructed and characterized in this work. The MCMHF membrane based on reduction-tolerant and CO2-stable SrFe0.8Nb0.2O3-δ (SFN) oxide not only possesses a good mechanical strength, but also has a high ox...
متن کاملCO2‐Tolerant SrFe0.8Nb0.2O3−δ−Carbonate Dual-Phase Multichannel Hollow Fiber Membrane for CO2 Capture
Ceramic−carbonate dual-phase membranes have attracted a lot of attention because of the emission of CO2 and environmental problems. In this study, a dense SrFe0.8Nb0.2O3−δ−carbonate dual-phase multichannel hollow fiber membrane has been successfully prepared via a phase inversion−sintering technique and impregnation. The morphology, crystal structure, phase stability, breaking load, and CO2 per...