Geometrical Control of 3C and 6H-SiC Nucleation on Low Off-Axis Substrates
نویسندگان
چکیده
Growth of 3C or 6H-SiC epilayers on low off-axis 6H-SiC substrates can be mastered by changing the size of the on axis plane formed by long terraces in the epilayer using geometrical control. The desired polytype can be selected in thick (~200 μm) layers of both 6H-SiC and 3C-SiC polytypes on substrates with off-orientation as low as 1.4 and 2 degrees. The resultant crystal quality of the 3C and the 6H-SiC epilayers, grown under the same process parameters, deteriorates when lowering the off-orientation of the substrate.
منابع مشابه
Advances in the molecular-beam epitaxial growth of artificially layered heteropolytypic structures of SiC
The controlled growth of SiC heteropolytypic structures consisting of hexagonal and cubic polytypes has been performed by solid-source molecular-beam epitaxy. On on-axis substrates, 4H/3C/4H–SiC~0001! and 6H/3C/6H–SiC~0001! structures were obtained by first growing the 3C–SiC layer some nanometer thick at lower substrate temperatures (T51550 K) and Si-rich conditions and a subsequent growth of ...
متن کاملKinetic surface roughening and wafer bow control in heteroepitaxial growth of 3C-SiC on Si(111) substrates
A thin, chemically inert 3C-SiC layer between GaN and Si helps not only to avoid the "melt-back" effect, but also to inhibit the crack generation in the grown GaN layers. The quality of GaN layer is heavily dependent on the unique properties of the available 3C-SiC/Si templates. In this paper, the parameters influencing the roughness, crystalline quality, and wafer bow are investigated and engi...
متن کاملProgress in 3C-SiC growth and novel applications
Recent research efforts in growth of 3C-SiC are reviewed. Sublimation growth is addressed with an emphasis on the enhanced understanding of polytype stability in relation to growth conditions, such as supersaturation and Si/C ratio. It is shown that at low temperature/supersaturation spiral 6H-SiC growth is favored, which prepares the surface for 3C-SiC nucleation. Provided the supersaturation ...
متن کاملMacrodefects in cubic silicon carbide crystals
Different sublimation growth conditions of 3C-SiC approaching a bulk process have been investigated with the focus on appearance of macrodefects. The growth rate of 3C-SiC crystals grown on 6H-SiC varied from 380 to 460 μm/h with the thickness of the crystals from 190 to 230 μm, respectively. The formation of macrodefects with void character was revealed at the early stage of 3C-SiC crystal gro...
متن کاملSublimation Growth and Performance of Cubic Silicon Carbide
Current advancement in electronic devices is so rapid that silicon, the semiconductor material most widely used today, needs to be replaced in some of the fields. Silicon carbide (SiC) is a wide band gap semiconductor satisfying requirements to replace silicon in devices operating at high power and high frequency at elevated temperature, and in harsh environments. Hexagonal polytypes of SiC, su...
متن کامل