Synthesis of silica nanoparticles from Vietnamese rice husk by sol–gel method

نویسندگان

  • Van Hai Le
  • Chi Nhan Ha Thuc
  • Huy Ha Thuc
چکیده

Silica powder at nanoscale was obtained by heat treatment of Vietnamese rice husk following the sol-gel method. The rice husk ash (RHA) is synthesized using rice husk which was thermally treated at optimal condition at 600°C for 4 h. The silica from RHA was extracted using sodium hydroxide solution to produce a sodium silicate solution and then precipitated by adding H2SO4 at pH = 4 in the mixture of water/butanol with cationic presence. In order to identify the optimal condition for producing the homogenous silica nanoparticles, the effects of surfactant surface coverage, aging temperature, and aging time were investigated. By analysis of X-ray diffraction, scanning electron microscopy, and transmission electron microscopy, the silica product obtained was amorphous and the uniformity of the nanosized sample was observed at an average size of 3 nm, and the BET result showed that the highest specific surface of the sample was about 340 m2/g. The results obtained in the mentioned method prove that the rice husk from agricultural wastes can be used for the production of silica nanoparticles.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Synthesis of Unsymmetrical Ethers Catalysed by Polyvinyl Sulfuric Acid & PVSA / Nano RH SiO2 as a Novel Solid Acid Nanocomposite

The methodology involves preparing polyvinyl sulfuric acid as a solid acid by simple mixing ofpolyvinyl alcohol with chlorosulfonic acid in CH2Cl2 at room temperature. The catalytic ability ofthe solid acid was investigated for the facile conversion of benzylic alcohols to the unsymmetricalethers with aliphatic alcohols in the presence of the solid acid. Results show that the solid acid isan ap...

متن کامل

Synthesis and Characterizations of Silica Nanoparticles by a New Sol-Gel Method

Silica nanoparticles were synthesized by chemical methods from tetraethylorthosilicate (TEOS), polyethylene glycol 5% and hydrochloric acid 0.001 N. The sol-gel process was applied for the preparation of nano silica gel. This method is hydrolysis and condensation reactions of TEOS as precursor of silica. The optimal synthesis conditions for the preparation of silica nanoparticles were obtained ...

متن کامل

The Synthesis and Characterization of Cobalt-Rice Husk Silica Nanoparticles

Spherical and needle-like cobalt nanoparticles incorporated on rice husk silica was synthesized by a simple, rapid and eco-friendly sol-gel route at room temperature. This was achieved by direct mixing of 20 wt.% Co with sodium silicate from rice husk under ambient conditions to form RH-20Co. The cobalt was found to be isomorphously substituted in the silica matrix. A good dispersion of cobalt ...

متن کامل

Synthesis of Pyranopyrazole Compounds Using Heterogeneous Base Catalyst Based on 1,3,5-Triazine-2,4,6-Triamine Modified Nano Rice Husk Silica

In the current study, amorphous silica nanoparticles were easily extracted from rice husk ash. The target composite was synthesized by the direct incorporation of chloropropyl groups through the condensation of nanosilica and 3-chloropropyl trimethoxysilane and then grafting of 1,3,5-triazine-2,4,6-triamine (Melamine) onto the propyl groups by the simple nucleophilic substitution reaction (RHA@...

متن کامل

Synthesis and characterization of the Pt/SiO2 nanocomposite by the sol-gel method

The silica supported platinum nanoparticles was synthesized by using the sol-gel method. The possibility of using diamminedinitro platinum (II) as Pt precursor and effect of metal precursor concentration on the final Pt nanoparticle size was investigated. A stable silica sol was prepared via hydrolysis of tetraethyl orthosilicate (TEOS) as a metal alcoxide and condensation reaction. Subsequentl...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 8  شماره 

صفحات  -

تاریخ انتشار 2013