Hardness and Composition of Solution-Treated Ag-Pd-Cu-Au Alloy Microstructures
نویسندگان
چکیده
An Ag-Pd-Cu-Au casting alloy was subjected to solution treatment at various temperatures. The dynamic hardness of each resultant microstructure and the Vickers hardness of the whole alloy were measured to investigate their relationship with changes in metal and crystal structure of the alloy and microstructural elemental concentration. The samples following solution treatment at 650, 700, 750, and 800 C consisted of a fine-layer structure (Structure A), a rough-layer structure (Structure B), and an island-like structure (Structure C). Structures A and B, after treatment at 850 C, were indistinguishable. The composition of Structure A was very similar to that of the alloy. Structures B and C were Ag-rich/Pd-poor/Cu-poor and Ag-poor/Pd-rich/Cu-rich, respectively. The composition of Structures B and C approached that of Structure A with increasing treatment temperature. The dynamic hardness, which was highest in Structure A, lower in Structure C, and lowest in Structure B, increased with increasing treatment temperature. These findings suggest that solid solution strengthening, due to elemental diffusion between structures during heating, contributes to hardening at elevated solution treatment temperatures. [doi:10.2320/matertrans.MRA2008191]
منابع مشابه
Sulfuration resistance of five experimental Ag-Pd-Au-Cu alloys with low Pd content of 10 or 12%.
Commercial Ag-based alloy (46Ag-20Pd-12Au-20Cu alloy) is widely used in Japan as a casting alloy. As opposed to the commercial composition, we prepared five experimental Ag-based alloys with reduced Pd content of 10 or 12%, increased Au content of 20 to 30%, and reduced Cu content of 12 to 20%. We then evaluated their sulfuration resistance by analyzing cast specimen surfaces dipped in 0.1% Na2...
متن کاملSpinodal decomposition related to age-hardening and cuboidal structures in a dental low-carat gold alloy with relatively high Cu/Ag content ratio
A dental Au–Ag–Cu–Pd alloy with a relatively low Au content and a high Cu/Ag content ratio was examined to determine the correlation between the microstructural changes by the spinodal decomposition and age-hardening behaviour using a hardness test, X-ray diffraction study, field emission scanning electron microscopy and energy-dispersive X-ray spectrometry. Separation of the parent α0 phase oc...
متن کاملEffects of Current Stressing on the Grain Structure and Mechanical Properties of Ag-Alloy Bonding Wires with Various Pd and Au Contents
Ag-alloy bonding wires containing various Pd and Au elements and traditional 4 N Au and Pd-coated 4 N Cu bonding wires were stressed with a current density of 1.23 ˆ 105 A/cm2 in air. The amounts of annealing twins in the Ag-alloy wires were much higher than those in Au and Pd-coated Cu wires. The percentages of twinned grains in these Ag-alloy wires increased obviously with current stressing. ...
متن کاملPrecipitation hardening in a dental low-gold alloy.
Age-hardening characteristics in a dental low-gold alloy composed of 40.0 wt% Au-35.0 wt% Ag-7.9 wt% Pd-7.0 wt% Cu-5.0 wt% In-3.5 wt% Zn-1.5 wt% Sn, were investigated by means of the hardness test, XRD study, SEM observations and EPMA. The following results were obtained. The age-hardening was characterized by a precipitation of Cu-rich alpha2 phase in the a phase. The softening that occurred f...
متن کاملAlloy Oxidation and Porcelain Fused to Alloy Interaction in Noble Alloy Systems
The oxidation and porcelain fusion characteristics of noble alloys containing a variety of minor oxidizable elements, including Cu, Sn, In, Ga, Mn, and Fe were investigated. Four porcelain alloys systems: a Pd-base alloy (Naturelle}, two Pd-Ag-based alloys (Jelstar and Acclaim}, and a high Au-alloy (SMG-3) were examined by scanning electron microscopy and energy dispersive spectroscopy after be...
متن کامل