Spatial control of InGaN luminescence by MOCVD selective epitaxy
نویسندگان
چکیده
Selective epitaxial growth of InGaN alloys was performed by metalorganic chemical vapor deposition (MOCVD). Templates consisted of arrays of circular etched holes in a SiO 2 mask layer, with pre-grown GaN hexagonal pyramid structures. The room temperature (300 K) photoluminescence (PL) peak wavelength increased with increasing maskopening spacing for a constant mask-opening diameter. For 5 lm diameter pyramids, peak PL wavelengths ranged from 457 to 505 nm for mask opening spacings of 6 to 13 lm, compared to PL peak wavelength of 420 nm for a planar reference sample. ( 1998 Elsevier Science B.V. All rights reserved.
منابع مشابه
Origin of broad luminescence from sitecontrolled InGaN nanodots fabricated by selectivearea epitaxy
We investigated the origin of broad luminescence observed from an array of site-controlled InGaN nanodots grown by selective area epitaxy (SAE). Epitaxially grown site-controlled nanodots with lateral dimensions <50 nm and an array density of 10 cm 2 have been studied. During the nanoscale SAE, incorporation of adatoms from the SiO2 mask has greater relative importance, resulting in a non-unifo...
متن کاملDesign and characteristics of staggered InGaN quantum-well light-emitting diodes in the green spectral regime
Staggered InGaN quantum wells (QWs) are investigated both numerically and experimentally as improved active region for light-emitting diodes (LEDs) emitting at 520–525 nm. Based on a self-consistent six-band k.p method, band structures of both two-layer staggered InxGa12xN/InyGa12yN QW and three-layer staggered InyGa12yN/InxGa12xN/InyGa12yN QW structures are investigated as active region to enh...
متن کاملLuminescence Properties of Epitaxially Grown GaN and InGaN Layers Around ZnO Nanopillars
GaN and InGaN layers grown around ZnO nanopillars by metalorganic vapor phase epitaxy (MOVPE) are investigated by means of photoluminescence (PL) and locally resolved cathodoluminescence (CL). A multi layer growth process involving deposition at different growth conditions in a step-wise manner has been employed for the coaxially grown GaN. Then InGaN/GaN quantum wells and barriers have been de...
متن کاملBroadband full-color monolithic InGaN light-emitting diodes by self-assembled InGaN quantum dots
We have presented broadband full-color monolithic InGaN light-emitting diodes (LEDs) by self-assembled InGaN quantum dots (QDs) using metal organic chemical vapor deposition (MOCVD). The electroluminescence spectra of the InGaN QDs LEDs are extremely broad span from 410 nm to 720 nm with a line-width of 164 nm, covering entire visible wavelength range. A color temperature of 3370 K and a color ...
متن کاملCoaxial InGaN Epitaxy Around GaN Nano-tubes: Tracing the Signs
This work focuses on investigations of the luminescence properties of coaxial InGaN layers around single GaN nano-tubes on top of GaN micro-pyramids. The nano-tube structure was formed after the controlled desorption of ZnO nano-pillar templates during the coaxial GaN epitaxy. An intense and broad photoluminescence (PL) peak centered around 2.85 eV is attributed to transitions from a shallow do...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 1998