Tundish Nozzle Clogging – Application of Computational Models
نویسندگان
چکیده
Clogging of the tundish nozzle is a major castability problem in continuous casting of steel for several reasons. Firstly, clogging increases the frequency of operation disruptions to change nozzles or tundishes or even to stop casting. These extra transitions increase operating cost, decrease productivity, and lower quality. Secondly, clogging can lead directly to a variety of quality problems. Clogs change the nozzle flow pattern and jet characteristics exiting the ports, which can disrupt flow in the mold, leading to surface defects in the steel product and even breakouts. Dislodged clogs also disturb the flow and either become trapped in the steel or change the flux composition, leading to defects in either case. Quality problems also arise from the mold level transients which occur as the flow control device compensates for the clogging.
منابع مشابه
Clogging in Continuous Casting Nozzles
Nozzle clogging is a serious productivity and quality problem in continuous casting. This work reviews the causes, effects, and solutions to clogging in continuous casting nozzles. The results of a one-dimensional, steady state analysis of the heat loss from the molten steel stream through the nozzle wall are discussed. The analyses show that steel may freeze within the clog matrix for a relati...
متن کاملTransient Turbulent Flow Simulation with Water Model Validation and Application to Slide Gate Dithering
Slide gate dithering can reduce nozzle clogging and sticking during continuous casting, but also influences transient flow in the mold and meniscus level fluctuations. In this work, a semi-analytical model was first developed and validated to predict nozzle flow rate from slide-gate opening position. A transient CFD model of 3-D turbulent flow was then validated with surface velocity measuremen...
متن کاملModeling of Continuous-Casting Defects Related to Mold Fluid Flow
The quality of continuous-cast steel is greatly influenced by fluid flow in the mold, particularly at the meniscus. Recent examples of computational model applications at the University of Illinois are presented to investigate the formation of several different types of defects related to flow phenomena. The amount of gas injection into the tundish nozzle to avoid air aspiration is quantified b...
متن کاملFlow Field Characteristics of an Aerospike Nozzle Using Different Turbulence Models
To improve the calculation of the flow properties of an aerospike nozzle, different turbulence models were investigated in this study. The primary shape of the nozzle plug is determined through utilizing an approximate method. The flow field is, then, simulated using the Navier-Stokes equations for compressible flows. The commercial computational fluid dynamics code Fluent is used to simulate t...
متن کاملModeling and Removal of Inclusions in Continuous Casting
Continuous casting is the central process phase with strong influence on the final quality of the steel products. Several different models for continuous casting have been developed at the Laboratory of Metallurgy at Helsinki University of Technology (TKK) concerning e.g. fluid flow, heat transfer, thermodynamic equilibria and statistical approaches. In this paper the inhouse solidification mod...
متن کامل