Direct formation of peritectic phase but no primary phase appearance within Ni83.25Zr16.75 peritectic alloy during free fall
نویسندگان
چکیده
Ni83.25Zr16.75 peritectic alloy was containerlessly solidified in a drop tube. When the droplet diameter exceeds a critical value (Dcrit), Ni7Zr2 phase primarily solidifies, followed by the peritectic reaction of Ni7Zr2 + L → Ni5Zr. Once the droplet diameter is smaller than the critical value (Dcrit), peritectic phase Ni5Zr directly solidifies from the undercooled melt by completely suppressing the nucleation and growth of Ni7Zr2 phase, which is ascribed to high undercooling and cooling rate. Additionally, peritectic phase Ni5Zr grows equiaxially in the sample solidified in a DSC at a cooling rate of 0.167 K/s.
منابع مشابه
Evidence for the transition from primary to peritectic phase growth during solidification of undercooled Ni-Zr alloy levitated by electromagnetic field
The Ni83.25Zr16.75 peritectic alloy was undercooled by electromagnetic levitation method up to 198 K. The measured dendritic growth velocity shows a steep acceleration at a critical undercooling of ΔTcrit = 124 K, which provides an evidence of the transition of the primary growth mode from Ni7Zr2 phase to peritectic phase Ni5Zr. This is ascertained by combining the temperature-time profile and ...
متن کاملRapid solidification behavior of Zn-rich Zn–Ag peritectic alloys
Rapid solidification experiments, including laser remelting, melt-spinning and wedge casting, were carried out to investigate the rapid solidification behavior of Zn-rich Zn–Ag peritectic alloys containing up to 9.0 at% Ag. For comparison, Bridgman solidification experiments of the same alloys were also carried out for growth velocities ranging from 0.02 to 4.82 mm/s, which were lower than that...
متن کاملPeritectic phase transformation in the Fe–Mn and Fe–C system utilizing simulations with phase-field method
The present investigation focuses on the solidification of peritectic binary alloys in the systems Fe–Mn and Fe–C by utilizing phase-field simulations. Isothermal and directional solidification conditions were simulated with this approach and the following aspects were investigated: the phases evolution during the peritectic transformation close to the peritectic temperature for the Fe–Mn alloy...
متن کاملEffect of a weak transverse magnetic field on the microstructure in directionally solidified peritectic alloys
Effect of a weak transverse magnetic field on the microstructures in directionally solidified Fe-Ni and Pb-Bi peritectic alloys has been investigated experimentally. The results indicate that the magnetic field can induce the formation of banded and island-like structures and refine the primary phase in peritectic alloys. The above results are enhanced with increasing magnetic field. Furthermor...
متن کاملDetachment of secondary dendrite arm in a directionally solidified Sn-Ni peritectic alloy under deceleration growth condition
In order to better understand the detachment mechanism of secondary dendrite arm during peritectic solidification, the detachment of secondary dendrite arm from the primary dendrite arms in directionally solidified Sn-36at.%Ni peritectic alloys is investigated at different deceleration rates. Extensive detachment of secondary dendrite arms from primary stem is observed below peritectic reaction...
متن کامل