Properties-Adjustable Alumina-Zirconia Nanolaminate Dielectric Fabricated by Spin-Coating
نویسندگان
چکیده
In this paper, an alumina-zirconia (Al₂O₃-ZrO₂) nanolaminate dielectric was fabricated by spin-coating and the performance was investigated. It was found that the properties of the dielectric can be adjusted by changing the content of Al₂O₃/ZrO₂ in nanolaminates: when the content of Al₂O₃ was higher than 50%, the properties of nanolaminates, such as the optical energy gap, dielectric strength (Vds), capacitance density, and relative permittivity were relatively stable, while the change of these properties became larger when the content of Al₂O₃ was less than 50%. With the content of ZrO₂ varying from 50% to 100%, the variation of these properties was up to 0.482 eV, 2.12 MV/cm, 135.35 nF/cm², and 11.64, respectively. Furthermore, it was demonstrated that the dielectric strength of nanolaminates were influenced significantly by the number (n) of bilayers. Every increment of one Al₂O₃-ZrO2 bilayer will enhance the dielectric strength by around 0.39 MV/cm (Vds ≈ 0.86 + 0.39n). This could be contributed to the amorphous alumina which interrupted the grain boundaries of zirconia.
منابع مشابه
Fibrous Monolithic Ceramics: I , Fabrication, Microstructure, and Indentation Behavior
Monolithic ceramics have been fabricated from coated green fibers to create fibrous microstructures. The fibrous monoliths consist of high aspect ratio polycrystalline regions (cells) of a primary phase separated by thin secondphase regions (cell boundaries) designed to improve fracture resistance. The cells are the remnants of the green fiber which consists of ceramic powder and a polymer bind...
متن کاملCrystallization Behavior and Mechanical Properties of In-situ Alumina-Zirconia Composite Bodies
In-situ alumina-zirconia composite bodies were fabricated by heat treatment of gibbsite-zircon-kaolinite mixture at 1450℃. The current research investigated crystallization behavior and mechanical properties of the mentioned mixture in the presence of 5 wt.% MgO as an additive. X-ray diffraction (XRD) results showed that alumina, zirconia, and magnesium aluminosilicate were crystallized during ...
متن کاملThreshold strength and residual stress analysis of zirconia–alumina laminates
We dedicate this work to Wolfgang Pompe, a very good friend and a good friend of the Materials Faculty at UCSB where he and his wife, Gisela, shared their lives and fellowship. Three different zirconia–alumina laminates, AZ50, AZ80, and AZ95, were fabricated via tape-casting thick Zr(3Y)O2 layers, dip-coating the zirconia tapes in a slurry containing a mixture of zirconia and alumina, stacking ...
متن کاملGrowth of nanolaminate structure of tetragonal zirconia by pulsed laser deposition
Alumina/zirconia (Al2O3/ZrO2) multilayer thin films were deposited on Si (100) substrates at an optimized oxygen partial pressure of 3 Pa at room temperature by pulsed laser deposition. The Al2O3/ZrO2 multilayers of 10:10, 5:10, 5:5, and 4:4 nm with 40 bilayers were deposited alternately in order to stabilize a high-temperature phase of zirconia at room temperature. All these films were charact...
متن کاملElaboration of Alumina-Zirconia Composites: Role of the Zirconia Content on the Microstructure and Mechanical Properties
Alumina-zirconia (AZ) composites are attractive structural materials, which combine the high hardness and Young's modulus of the alumina matrix with additional toughening effects, due to the zirconia dispersion. In this study, AZ composites containing different amounts of zirconia (in the range 5-20 vol %) were prepared by a wet chemical method, consisting on the surface coating of alumina powd...