Recent studies of internal and surface nucleation in silicate glasses

نویسندگان

  • Edgar D. Zanotto
  • Vladimir M. Fokin
چکیده

This article reviews recent ­ ndings on internal and surface nucleation in silicate glasses. The internal homogeneous nucleation rates sharply decrease and the induction times increase with the Tg=TL ratio (Tg is the glass-transition temperature and TL is the liquidus temperature). Only systems that have Tg=TL < 0:58 display measurable internal nucleation rates on a laboratory time-scale. Numerous tests of the classical nucleation theory have demonstrated that the theory fails to describe nucleation rates in glasses quantitatively. Possible explanations for this failure are tested and discussed. Surface nucleation depends strongly on the surface quality, e.g. tips, cracks and scratches, elastic stresses, foreign particles and surrounding atmosphere. The mechanisms of surface nucleation are still not fully understood, but some of the key factors are now known and the surface-nucleation density can thus be controlled for the development of sintered glasses or glass ceramics.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Crystal nucleation in silicate glasses: the temperature and size dependence of crystal/liquid surface energy

The most basic assumption of the classical nucleation theory (CNT) is to treat nucleus/liquid surface energy, r, as a macroscopic property having a value equal to that of a planar interface, r1. Therefore, when the CNT is used to analyze experimental data, the size dependence of surface energy is often neglected. To date, there has been no reliable method to measure the surface energy of the nu...

متن کامل

Transient Nucleation in Glasses

r(NJ Nucleation rates in condensed systems are frequently not at their steady state values. Such time dependent (or transient) nucleation is most clearly observed in devitrification studies of metallic and silicate glasses. The origin of transient nucleation and its role in the formation and stability of desired phases and microstructures are discussed. Numerical models of nucleation in isother...

متن کامل

Heterogeneous crystal nucleation on bubbles in silicate melt

Experiments reported herein document heterogeneous crystal nucleation on bubbles in supercooled lithium disilicate melt. Crystalline lithium disilicate (Li2Si2O5) nucleated and grew on small bubbles (;1 mm) with a one-to-one correspondence between the number of bubbles and crystals (ranging from ,102 to ;105 bubbles/mm3). Crystals grew on large bubbles (.100 mm) only in samples fused in N2, sug...

متن کامل

Preparation and Studies of Structural and Thermo-mechanical Aspects of Some Special Glasses and Glass-ceramics

Glasses and glass-ceramics (GCs) used for sealing, coating and high voltage applications belong to a special class of materials in which among other requirements, matching of thermal expansion coefficient with that of metal as closely as possible up to set temperature is an important consideration. In this paper I shall concentrate on some indigenous efforts carried out in my laboratory on the ...

متن کامل

Determination of the Nucleation and Crystallization Parameters for Making Nanoporous Titanium Phosphate Glass-ceramics

Nanoporous glass-ceramics were prepared with composition 45CaO-25TiO2-35P2O5 (mol%). Two molar percent of Na2O was added as a flux to the composition. With the aforementioned composition, glass melted and crystallized into glass-ceramics containing β-Ca3(PO4)2 and CaTi4(PO4)6 as the main phases. The differential thermal analysis (DTA) was conducted to determine the suitable temperatures f...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2003