Characterization of ferrite nanoparticles for preparation of biocomposites
نویسندگان
چکیده
Ferrite nanoparticles with nominal composition Me0.5Fe2.5O4 (Me = Co, Fe, Ni or Mn) have been successfully prepared by the wet chemical method. The obtained particles have a mean diameter of 11-16 ± 2 nm and were modified to improve their magnetic properties and chemical activity. The surface of the pristine nanoparticles was functionalized afterwards with -COOH and -NH2 groups to obtain a bioactive layer. To achieve our goal, two different modification approaches were realized. In the first one, glutaraldehyde was attached to the nanoparticles as a linker. In the second one, direct bonding of such nanoparticles with a bioparticle was studied. In subsequent steps, the nanoparticles were immobilized with enzymes such as albumin, glucose oxidase, lipase and trypsin as a test bioparticles. The characterization of the nanoparticles was acheived by transmission electron microscopy, X-ray diffraction, energy dispersive X-ray and Mössbauer spectroscopy. The effect of the obtained biocomposites was monitored by Fourier transform infrared spectroscopy. The obtained results show that in some cases the use of glutaraldehyde was crucial (albumin).
منابع مشابه
Preparation and Characterization of Manganese Ferrite Nanoparticles via Co-precipitation Method for Hyperthermia
In this work, Mn ferrite nanopowders were prepared by co-precipitation method and were characterized. Phase identification of the nanopowders was performed by X-ray diffraction method and the mean particle size of the nanopowders was calculated by Scherrer's formula, using necessary corrections. Magnetic parameters of the prepared nanopowders were measured by a vibrating sample magnetome...
متن کاملPreparation of Promoted Ni0.1Co0.9Fe2O4 Ferrite Nanoparticles and Investigation of Its Catalytic Activity on Decomposition of H2O2 and Optical Characterization of Pure Ni0.1Co0.9Fe2O4
Pure and ZnO-doped Ni0.1Co0.9Fe2O4 catalyst were prepared by co-precipitation method and thermal decomposition in air calcinated at 400-700°C and that treated with different amounts of zinc nitrate (0.46-2.25 w% ZnO). X-ray powder diffractometry, scanning electron microscopy (SEM) and BET analysis of nitrogen adsorption isotherms investigated the crystalline bulk structure and the surface area ...
متن کاملPreparation of Promoted Ni0.1Co0.9Fe2O4 Ferrite Nanoparticles and Investigation of Its Catalytic Activity on Decomposition of H2O2 and Optical Characterization of Pure Ni0.1Co0.9Fe2O4
Pure and ZnO-doped Ni0.1Co0.9Fe2O4 catalyst were prepared by co-precipitation method and thermal decomposition in air calcinated at 400-700°C and that treated with different amounts of zinc nitrate (0.46-2.25 w% ZnO). X-ray powder diffractometry, scanning electron microscopy (SEM) and BET analysis of nitrogen adsorption isotherms investigated the crystalline bulk structure and the surface area ...
متن کاملSynthesis and Characterization of Nickel Zinc Ferrite Nanoparticles
In this research nickel zinc ferrite nanoparticles with composition of Ni1-xZnxFe2O4 (where x=0, 0.3, 0.7, 1) were synthesized by a sol-gel method at 600 °C for 5 hours. The structure of nanoparticles was studied using X-ray diffraction pattern. The lattice parameter of ferrite nanoparticles was calculated and indicates lattice constant of nanoparticl...
متن کاملSynthesis and Characterization of Chitosan Coated Manganese Zinc Ferrite Nanoparticles as MRI Contrast Agents
Manganese zinc ferrite nanoparticles (MZF NPs) were synthesized by using a direct, efficient and environmental friendly hydrothermal method. To improve the colloidal stability of MZF NPs for biomedical applications, NPs were coated with chitosan by ionic gelation technique using sodium tripolyphosphate (TPP) as crosslinker. The synthesized NPs were characterized by X ray diffraction (XRD) analy...
متن کامل