Structure and electrical properties of sputtered TiO2/ZrO2 bilayer composite dielectrics upon annealing in nitrogen
نویسندگان
چکیده
The high-k dielectric TiO2/ZrO2 bilayer composite film was prepared on a Si substrate by radio frequency magnetron sputtering and post annealing in N2 at various temperatures in the range of 573 K to 973 K. Transmission electron microscopy observation revealed that the bilayer film fully mixed together and had good interfacial property at 773 K. Metal-oxide-semiconductor capacitors with high-k gate dielectric TiO2/ZrO2/p-Si were fabricated using Pt as the top gate electrode and as the bottom side electrode. The largest property permittivity of 46.1 and a very low leakage current density of 3.35 × 10-5 A/cm2 were achieved for the sample of TiO2/ZrO2/Si after annealing at 773 K.
منابع مشابه
Sonosynthesis and Characterization of TiO2/ZrO2 Nanocomposite and Photocatalytic degradation of Congo red Dye under UV Light
NanoTiO2 , nanoZrO2 and TiO2 /ZrO2 nanocomposite were prepared via sol gel method by using ultrasonic irradiation. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4 and titanium tetra 2-propoxide was diluted by 2-propanol and deionized water The TiO2 /ZrO2 nanocomposite was synthesized from directly mixing Titanium dried gel into Zirconium gel. The reaction mixture w...
متن کاملThe Impact of Current Density of Electroplating on Microstructure and Mechanical Properties of Ni-ZrO2-TiO2 Composite Coating
Metallic composite coatings with ceramic particles can be used to improve the mechanical and corrosion properties of steel. In the present research, Ni-ZrO2-TiO2 composite coating was fabricated on AISI 430 stainless steel through the electrodeposition method. The effect of the current density of electroplating (15, 17, 20, and 23 mA.cm-2)was investigated on the...
متن کاملImproved Thermal Stability of NiSi Nanolayer in Ni-Si Co-sputtered Structure
Electrical, structural and morphological properties of Ni silicide films formed in Ni(Pt 4at.% )/Si(100) and Ni0.6Si0.4(Pt4at.% )/Si(100) structures at various annealing temperatures ranging from 200 to 1000 oC were studied. The Ni(Pt) and Ni0.6Si0.4(Pt) films with thickness of 15 and 25 nm were deposited by RF magnetron co-sputtering method, respectively. The annealing process of the structur...
متن کاملThe effect of pH on the morphology and polarization resistance of Ni-P-TiO2-ZrO2 composite coating
Nickel field composite coatings have a high ability to improve surface properties, such as increased corrosion resistance and abrasion resistance. In this study, Ni-P-TiO2-ZrO2 composite coating on AISI 316L steel substrate was deposited by direct current flow method and the effects of different pH 3, 3.5, 4 and 4.5 on coating morphology and corrosion resistance were investigated. Scanning elec...
متن کاملEffect of Annealing Temperature on Structural, Electrical and Optical Properties of TiO2 Nanopowder
TiO2 nanopowder is prepared by simple sol-gel method using starting material as titanium isopropoxide with methanol and annealed at 600°C, 700°C and 800°C for 1 hour in air. X-ray diffraction pattern revealed the presence of both anatase and rutile phase in TiO2 specimens annealed at different temperatures. It is observed that the content of rutile phase and crystallite size increases with incr...
متن کامل