Cementitious bond degradation during cyclic shear loading, studied by contact electrical resistance measurement
نویسندگان
چکیده
Degradation of the cementitious bond between steel rebar and concrete and that between old and new mortar under cyclic shear loading was observed nondestructively by measuring the contact electrical resistance of the joint. Degradation, which caused a decrease in bond strength but no visual damage, was indicated by an abrupt increase in the resistance at a small fraction of the fatigue life. Bond failure was also accompanied by an abrupt increase in resistance. C © 2001 Kluwer Academic Publishers
منابع مشابه
مقایسه تأثیر نوع دندان مصنوعی و Cyclic loading بر میزان استحکام باند در آکریل بیس دنچر خودبهخود پلیمریزه شونده
Background and Aims: Failure of bonding between artificial teeth and denture base material is a considerable problem for patients who wear dentures. According to the different impact of artificial teeth and different information about resistance force of mastication and also with deficiency in researchs, this study was designed to compare the bond strength of composite and acrylic artificial te...
متن کاملBond Deformability of Reinforced Concrete Members
The usual earthquake resistant design philosophy of ductile frame buildings allows the beams to form plastic hinges adjacent to beam-column connections. In order to carry out this design philosophy, the ultimate bond or shear strength of the beam should be greater than the flexural yielding force and should not degrade before reaching its required ductility. The behavior of RC members dominated...
متن کاملCementitious Composites Engineered with Embedded Carbon Nanotube Thin Films for Enhanced Sensing Performance
Cementitious composites such as concrete pavements are susceptible to different damage modes, which are primarily caused by repeated loading and long-term deterioration. There is even greater concern that damage could worsen and occur more frequently with the use of heavier vehicles or new aircraft carrying greater payloads. Thus, the objective of this research is to engineer cementitious compo...
متن کاملCyclic Loading Tests for Cold-Formed Steel Wall Frames with Lightweight Concrete
Lightweight steel framing is a method in housing and construction that have been widely used in lightweight steel construction. In this method, the structure is built by cold formed steel elements. They are cost-effective, light, and easy to assemble. However, the performance of lateral load resisting systems in cold-formed steel structures specially the behavior of cold-formed steel shear wall...
متن کاملInclined Fiber Pullout from a Cementitious Matrix: A Numerical Study
It is well known that fibers improve the performance of cementitious composites by acting as bridging ligaments in cracks. Such bridging behavior is often studied through fiber pullout tests. The relation between the pullout force vs. slip end displacement is characteristic of the fiber-matrix interface. However, such a relation varies significantly with the fiber inclination angle. In the curr...
متن کامل