Effects of fibers on the color change and stability of resin composites after accelerated aging.
نویسندگان
چکیده
Composite resins were reinforced with glass and polyethylene fibers in this study, and the effect of fiber reinforcement on the color change of composite resins was investigated. After accelerated aging, the effect of fiber reinforcement on the color stability of composite resins was also examined. There were three experimental groups (n=12 disks per group): non-fiber-reinforced composite (non-FRC control), polyethylene fiber (Ribbond-THM)-reinforced composite, and glass fiber (everstick NET)-reinforced composite. According to the critical remarks of color change of National Bureau of Standarts (NSB), glass fiber-reinforced anterior composites showed trace color change and polyethylene-fiber reinforced composites showed slight color change before accelerated aging. After accelerated aging, both control and fiber-reinforced composite groups showed noticeable color change. It was concluded that both the types of fiber reinforcement and composite resin influenced the color change of fiber-reinforced composite resins.
منابع مشابه
Effect of Aging on the color stability of bleached shade resin composite (invitro)
Background and Aim: One of the most noticeable problems of composite restorations is color change of them over the time Due to this the most important advantage of composites which is providing esthetic is gone, so restorations need to be changed.The purpose of this study is to evaluate the effect of aging on color stability of two types of Bleached shade composites. Materials and methods: I...
متن کاملEffect of Accelerated Aging on the Color Stability of Light-cured Res-in Cement and Flowable Composite Through Porcelain Laminate Veneer
Background and Aim: Changing the color of resin luting cements could affect the aesthetic appearance of thin porcelain veneer. The aim of this in vitro study was to evaluate the effect of artificially accelerated aging on color stability of light-cured resin cement and flowable composite as a luting agent through the porcelain veneer. Materials and Methods: This experimental study was carried ...
متن کاملInfluence of Light-Curing Units on Color Stability of Composite Resins After Aging
Background and Aim: The use of composite restorations has increased in recent years. One of the most important problems with composite restorations is the loss of consistency between the composite and tooth color, which in most cases requires replacement. Materials and Methods: In this study, the color stability of 40 disc-shaped specimens (10 mm in diameter and 2 mm in height) from two types ...
متن کاملEffects of different polishing methods on color stability of resin composites after accelerated aging.
The purpose of this study was to evaluate the effect of polishing procedures on the color stability of different types of composites after aging. Forty disk-shaped specimens (Ø10×2 mm) were prepared for each composite resin type (an ormocer, a packable, a nanohybrid, and a microhybrid) for a total of 160 specimens. Each composite group was divided into four subgroups according to polishing meth...
متن کاملAccelerated Heat Aging Study of Phenolic/Basalt Fiber Reinforced Composites
One of the greatest impediments to use polymer-matrix composites is their susceptibility to degradation when exposed to the elevated temperatures and the limited knowledge on the thermal and mechanical properties of these composites at such temperatures. The objective of this study is to evaluate the effects of accelerated heat aging on the tensile properties of the Woven Basalt/Phenolic (WBP) ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Dental materials journal
دوره 31 5 شماره
صفحات -
تاریخ انتشار 2012