Study of MgB2 ultra-thin films in submicron size bridges
نویسندگان
چکیده
We discuss a custom built hybrid physical chemical vapour deposition (HPCVD) system for MgB2 ultra-thin film deposition: construction, deposition process development, and optimization. Achieved films on SiC substrates have a critical temperature (Tc) ranging from 35K (10nm thick films) to 41K (40nm thick films). The 20nm thick unpatterned film had a room temperature resistivity of 13μΩ·cm, whereas it becomes 50μΩ·cm in sub-micrometer size bridges with a critical current density Jc (4.2K) up to 1.2×108A/cm2. The lower value of resistivity corresponds to the higher of both Tc and Jc. The surface roughness, measured with an atomic force microscope (AFM), is approximately 1.5nm.
منابع مشابه
Growth and characterization of epitaxial ultra-thin NbN films on 3C-SiC/Si substrate for terahertz applications
We report on electrical properties and microstructure of epitaxial thin NbN films grown on 3C-SiC/Si substrates by means of reactive magnetron sputtering. A complete epitaxial growth at the NbN/3C-SiC interface has been confirmed by means of high-resolution transmission electron microscopy (HRTEM) along with x-ray diffractometry (XRD). Resistivity measurements of the films have shown that the s...
متن کاملBroadband MgB2 Hot-Electron Bolometer THz Mixers operating up to 20K
We discuss performance of submicron size hotelectron bolometer (HEB) mixers made from thin MgB2 superconducting films. With a superconducting transition temperature of 30K, such THz mixers can operate with high sensitivity at temperatures up to 20K. Due to very small dimensions local oscillator (LO) power requirements are rather low. In the intermediate frequency (IF) band of 1-3GHz the double...
متن کاملMgB2 HEB Mixers at Operation Temperatures above Liquid Helium Temperature
In this paper we discuss results of MgB2 thin films deposition for the hot-electron bolometer (HEB) application. For this purpose a custom made hybrid physical-chemical vapour deposition (HPCVD) system was built. For films thicknesses d in the 15-45nm range the critical temperatures were from 34K to 40K. For bridges as narrow as 500nm the critical current density was >107A/cm2 indicating a high...
متن کاملStudy of MgB2 HEB mixers at THz frequencies
The terahertz (THz) range is very attractive for astronomical observations. Spectroscopy and photometry of remote space objects in the THz range allows for a study of their chemical composition, because this range covers rotational lines from simple molecules and electron transition lines from atoms and ions. Heterodyne receivers, due to their high spectral resolution, in the THz range allows f...
متن کاملEffective vortex pinning in MgB2 thin films
We discuss the pinning properties of MgB2 thin films grown by pulsed-laser deposition (PLD) and by electron-beam (EB) evaporation. Two mechanisms are identified that contribute most effectively to the pinning of vortices in randomly oriented films. The EB process produces low defected crystallites with a small grain size providing enhanced pinning at grain boundaries without any degradation of ...
متن کامل