Friction and Wear Behaviors of Gear Steel under Coupling of Rolling and Sliding
نویسنده
چکیده
In this paper, the gear material 20CrMnTi was selected as the research object. Friction and wear behavior was performed on the M2000 friction and abrasion tester. The friction and wear mechanisms of 20CrMnTi steel were discussed under coupling of rolling and sliding. The results show that damage of steel-steel couples under coupling of rolling and sliding is caused by the interaction of mechanical fatigue with dynamical phenomena of rolling and sliding friction. Lubrication directly determines the friction and wear behaviors. Under dry friction, the wear mechanisms of 20CrMnTi steel are mainly adhesive wear, abrasive wear, oxidation wear and fatigue pitting under dry friction. Under lubricating conditions, the wear mechanism of 20CrMnTi steel is mainly surface fatigue wear.
منابع مشابه
Effect of Coating Materials on Wear in Internal Gears
Theoretical and experimental investigation of wear during coupling in internal gears coated with various polymeric coating materials was performed in this study. In the theoretical part of the study, Archards’ wear formulation was adapted to internal gears and wear behavior in various conditions was determined. Moreover, a fatigue and wear testing apparatus having similar working principle with...
متن کاملDry Sliding Tribological Behavior of TC11 Titanium Alloy Subjected to the Ultrasonic Impacting and Rolling Process
The dry sliding friction and wear behaviors of TC11 titanium alloy subjected to the ultrasonic impacting and rolling process (UIRP) were studied in the present work. The microstructure of the deformation layer and the morphology of the worn surfaces were observed. The results clearly show that the wear performance of TC11 alloy after UIRP is better than that of TC11 alloy before UIRP under the ...
متن کاملPin-on-Disc Study of Tribological Performance of Standard and Sintered Gear Materials Treated with Triboconditioning Process: Pre-treatment by Pressure-induced Tribo-film formation
Coating is one of the innovative approaches used to improve the wear resistance and load-carrying capacity of surfaces in rolling-sliding contact, such as gears and rolling element bearings. In this study, the tribological performance of standard gear material (EN 16MnCr5) and two kinds of powder metallurgy (PM) gear material (Distaloy AQ + 0.2% C and Astaloy 85Mo +0.2% C) with and without trib...
متن کاملCharacterization of CrN/TiN PVD Coatings on 316L Stainless Steel
In order to further enhance tribological properties 316 Low carbon stainless steel (L SS) used on mechanical parts. CrN/TiN with DC magnetron sputtering sources was carried out on PVD 316 L SS. The micro structure of the CrN/TiN coatings were investigated by Scanning electron microscope (SEM), X-ray Diffraction (XRD) and tribology properties were investigated on a Pin on Disc friction and wear ...
متن کاملThe Effect to Epsilon Phase on the Friction and Wear of Nitrided Die Steels (RESEARCH NOTE)
In this paper, the wear resistance and antifriction of epsilon phase layer and diffusion layer of gas nitrided D2 steel and M2 steel have been studied. The changes m wear mechanism of epsilon phase under the load from 20N to 200N are analysed. When the load is lighter than 100N, it is mainly oxidizing wear on friction surface. The adhesion, peeling off and abrasive wear appear on friction surfa...
متن کامل