Immobilization of Poly(1,1-dimethysilacyclobutane) by Means of Anionic Ring-Opening Polymerization on Organic Nanoparticles and Reinvestigation of Crystallization

In the present study, the synthesis of poly(1,1-dimethylsilacyclobutane) (PDMSB) by anionic ring opening polymerization (ROP) is reinvestigated, leading to narrowly distributed molar masses (polydispersities 1.04–1.15) in the range of 2.3 to 60 kg mol. Investigations of thermal behavior for low molar mass PDMSB revealed an untypical multiple peaks melting phenomenon, which at first glance, seems to be of the same origin as low molar mass poly(ethylene oxide)s. Small angle X-ray scattering (SAXS) and X-ray diffraction (XRD) measurements are done, proving the fast crystallization and subsequent recrystallization for investigated low molar mass samples. Synthetic attempts are expanded to the surface-initiated anionic ROP of 1,1-dimethylsilacyclobutane (DMSB) monomer from the surface of cross-linked polystyrene (PS) nanoparticles. Novel polycarbosilanes (PCS)/organic core/shell particles are obtained, which are investigated by using transmission electron microscopy (TEM) and dynamic light scattering (DLS) experiments. First insights into the crystallization behavior OPEN ACCESS Polymers 2013, 5 285 of surface-attached PDMSB chains reveal that crystallization seems to be hindered.