High molecular mass polyethylene aqueous latexes by catalytic polymerization.
نویسندگان
چکیده
Semicrystalline microparticles of high molecular mass polyethylene can be prepared as aqueous dispersions by catalytic emulsion polymerization of ethylene with a mini-emulsified catalyst precursor (D$\rm{\frown}$D=salicylaldimine, L=pyridine). Stable polymer latexes are formed.
منابع مشابه
Catalytic Ethylene Polymerization in Aqueous Emulsion : Catalyst Tailoring and Synthesis of Very Small Latex Particles
INTRODUCTION Emulsion polymerization yielding polymer latexes, is carried out on a vast scale. The use of water as a dispersion medium offers a unique combination of features, such as effective heat transfer, effective stabilization of polymer particles by surfactants, and environmental friendliness. By contrast to polymerization in solution or in the bulk, in emulsion polymerization a large po...
متن کاملRemote substituents controlling catalytic polymerization by very active and robust neutral nickel(II) complexes.
More than 70 million tons of polyethylene and polypropylene are produced annually. The majority is prepared by catalytic polymerization employing Ziegler or Phillips catalysts based on early transition metals. More recently, olefin polymerization by complexes of late transition metals has also received increasing attention. A major motivation is their higher tolerance towards polar reagents due...
متن کاملCatalytic Polymerization of Ethylene in Aqueous Emulsion with a Simple in Situ Catalyst
Catalytic polymerization of ethylene in aqueous emulsion by in situ catalysts based entirely on compounds commercially available from standard chemicals suppliers, namely a chlorinated derivative of 1,4-benzoquinone, triphenylphosphine, and bis(1,5-cyclooctadiene)nickel, is reported. Using miniemulsions of catalyst solutions in a small amount of hydrocarbon solvent for polymerization, stable di...
متن کاملNanocrystal Formation in Aqueous Insertion Polymerization
High molecular weight linear polyethylene, in the form of 7 nm thin single-lamella nanocrystals with a diameter of up to 200 nm, is generated via aqueous catalytic polymerization using the water-soluble catalyst precursor [κN,O-{2,6-(3′,5′-(F3C)2C6H3)2C6H3-NC(H)-(3,5-I2-2-OC6H2)}NiCH3{P(3-C6H4SO3Na)3}] (1-TPPTS). Studies under true pressure reactor conditions using a C-labeled catalyst precurs...
متن کاملSynthesis of high molecular weight polyethylene using FI catalyst
A FI Zr-based catalyst of bis[N-(3,5-dicumylsalicylidene)-2′,6′diisopropylanilinato]zirconium(IV) dichloride was prepared and used for polymerization of ethylene. The effects of reaction conditions on the polymerization were examined in detail. The increase in ethylene pressure and rise in polymerization temperature up to 35 oC were favorable for catalyst/MAO to raise the catalytic activity as...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Angewandte Chemie
دوره 40 16 شماره
صفحات -
تاریخ انتشار 2001