High-pressure synthesis, crystal chemistry and physics of perovskites with small cations at the A site.

نویسندگان

  • Alexei A Belik
  • Wei Yi
چکیده

ABO3 perovskites with small cations at the A site (A = Sc(3+), In(3+) and Mn(2+) and B = Al(3+) and transition metals) are reviewed. They extend the corresponding families of perovskites with A(3+) = Y, La-Lu, and Bi and A(2+) = Cd, Ca, Sr and Ba and exhibit the largest structural distortions. As a result of these large distortions, they show, in many cases, distinct structural and magnetic properties. These are manifested in: B-site-ordered monoclinic structures of ScMnO3 and 'InMnO3'; an unusual superstructure of ScRhO3 and InRhO3; antiferromagnetic ground states and multiferroic properties of Sc2NiMnO6 and In2NiMnO6; two magnetic transitions in ScCrO3 and InCrO3 with very close transition temperatures; a Pnma-to-P-1 structural transition and k = (½, 0, ½) magnetic ordering in ScVO3; and incommensurate magnetic ordering of Mn(2+) spins in metallic MnVO3. A large number of simple ScBO3, InBO3 and MnBO3 perovskites has not been synthesized yet, and the number of experimental and theoretical works on each known ScBO3, InBO3 and MnBO3 perovskites counts to only one or two (except for ScAlO3). The synthesis, crystal chemistry and physics of perovskites with small cations at the A site is an emerging field in perovskite science.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Generalized trends in the formation energies of perovskite oxides.

Generalized trends in the formation energies of several families of perovskite oxides (ABO3) and plausible explanations to their existence are provided in this study through a combination of DFT calculations, solid-state physics analyses and simple physical/chemical descriptors. The studied elements at the A site of perovskites comprise rare-earth, alkaline-earth and alkaline metals, whereas 3d...

متن کامل

Convectional hydrothermal synthesis of high-purity pesudo-cubic BaTi0.09Nb0.01O3 nanocrystals in rotary autoclave

Nano-sized BaTiO3 powders with particular Nb concentrations were prepared by Rotary- Hydrothermal (RH) method. Hydrothermal method was used at 180 °C for 5 hours with new Ti pressure and the teflon vessel was rotated at a speed of 160 rpm during the hydrothermal reaction. New hydrothermal method was used instead of previous solid state reaction for the system BaTiO3±Nb<sub...

متن کامل

Convectional hydrothermal synthesis of high-purity pesudo-cubic BaTi0.09Nb0.01O3 nanocrystals in rotary autoclave

Nano-sized BaTiO3 powders with particular Nb concentrations were prepared by Rotary- Hydrothermal (RH) method. Hydrothermal method was used at 180 °C for 5 hours with new Ti pressure and the teflon vessel was rotated at a speed of 160 rpm during the hydrothermal reaction. New hydrothermal method was used instead of previous solid state reaction for the system BaTiO3±Nb<sub...

متن کامل

Structure and cation distribution in perovskites with small cations at the A site: the case of ScCoO3

We synthesize ScCoO3 perovskite and its solid solutions, ScCo1-x Fe x O3 and ScCo1-x Cr x O3, under high pressure (6 GPa) and high temperature (1570 K) conditions. We find noticeable shifts from the stoichiometric compositions, expressed as (Sc1-xMx )MO3 with x = 0.05-0.11 and M = Co, (Co, Fe) and (Co, Cr). The crystal structure of (Sc0.95Co0.05)CoO3 is refined using synchrotron x-ray powder di...

متن کامل

Synthesis and Characterization of Amine-modified Mesoporous SBA-15 for Carbon Dioxide Sequestration at High Pressure and Room Temperature (RESEARCH NOTE)

Amine-modified mesoporous SBA-15 adsorbent has been prepared by impregnation method using tetraethylenepentamine. The samples of this modified SBA-15 have been characterized by small angle X-ray scattering (SAXS), Scanning electron microscopy (SEM), Nitrogen adsorption-desorption isotherm and FT-IR. The adsorption capacity of CO2 on unmodified and modified samples were measured at high pressure...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Journal of physics. Condensed matter : an Institute of Physics journal

دوره 26 16  شماره 

صفحات  -

تاریخ انتشار 2014