Adhesion and Hardness Evaluation of Modified Silicone-Dammar as Natural Coating Materials
ثبت نشده
چکیده
Problem statement: Dammar is a natural resin that used anciently in varnish production. The use of dammar natural resin in coating is limited by undesirable properties for application in coating where it is considered very brittle. Due to dammar's brittle nature, an aged dammar coating can be easily scratched or abraded. Approach: Dammar natural resin could be modified into SiliconeDammar by using a solvent in order to improve the coating’s mechanical properties. The modified Silicone-Dammar (SD) was coated on aluminum q-panel and adhesion was evaluated using cross hatch test, impact test and pull off test, while the hardness of coating was investigated by nano-indentation test. Results: Results from cross hatch test, impact test and pull off test show that coating material with 15% wt. of dammar (SD15) was the optimum composition which exhibits good adhesion of modified Silicone-Dammar to the metal substrate. SD15 also could be considered as a soft and flexible polymer coating with hardness value of 1.624 GPa after undergoing the nano-indentation test. Conclusion: A modified Silicone-Dammar coating system with varied compositions of dammar has been prepared and adhesion and hardness have been evaluated. It is found that 15% wt. of dammar in the coating material (SD15) exhibits good adhesion to aluminum substrate and soft and flexible in nature.
منابع مشابه
Haemocompatibility evaluation of DLC- and SiC-coated surfaces.
Diamond-like carbon (DLC) and silicon carbide (SiC) coatings are attractive because of low friction coefficient, high hardness, chemical inertness and smooth finish, which they provide to biomedical devices. Silicon wafers (Si(waf)) and silicone rubber (Si(rub)) plates were coated using plasma-enhanced chemical vapour deposition (PE-CVD) techniques. This article describes: 1- the characterizati...
متن کاملRoughness Model for Adhesion Testing of Pharmaceutical Coating Materials
Objective Roughness is the main parameter in interlocking bonding mechanism. Yet there is no model designed to evaluate the effect of surface roughness on adhesion of coating materials in pharmaceutical sciences. Materials and Methods In this study polymethyl metacrylate spherical beads with different sizes were poured into 10 mm mold, then it was pressed by hand screw and finally heated to 141...
متن کاملFEASIBILITY OF PRODUCING NANO STRUCTURED METALLIC AND NON-METALLIC COATINGS ON Al SUBSTRATE USING MECHANICAL COATING ROUTE
In this paper, the possibility of mechanical coating of aluminum with either Ni or SiC using planetary ball mill was studied. The Al substrate was fixed inside of the vial lid of a planetary ball mill filled with milling balls and starting powder. The phase analysis and crystallite size measurement of the coatings were carried out using X-ray diffraction (XRD) method. Scanning electron micro...
متن کاملLiquid-Infused Silicone As a Biofouling-Free Medical Material
There is a dire need for infection prevention strategies that do not require the use of antibiotics, which exacerbate the rise of multiand pan-drug resistant infectious organisms. An important target in this area is the bacterial attachment and subsequent biofilm formation on medical devices (e.g., catheters). Here we describe nonfouling, lubricant-infused slippery polymers as proof-of-concept ...
متن کاملBiomimetic modification of silicone tubes using sodium nitrite-collagen immobilization accelerates endothelialization.
Biomimetic coatings to increase endothelialization of blood-contacting materials in biomedical devices are promising to improve the biocompatibility of these devices. Although a stable extracellular matrix protein coating on a biomaterial's surface is a prerequisite for endothelial cell attachment, it also stimulates platelet adhesion. Therefore, antithrombotic additives, such as nitric oxide d...
متن کامل