The Catalytic Activity of Cu2O Microparticles
ثبت نشده
چکیده
Copper (I) oxide microparticles with the morphology of cubic and hollow sphere were synthesized with the assistance of surfactant as the shape controller. Both particles were then subjected to study the catalytic activity and observed the results of shape effects of catalysts on rate of catalytic reaction. The decolorizing reaction of crystal violet and sodium hydroxide was chosen and measured the decreasing of reactant with respect to times using spectrophotometer. The result revealed that morphology of crystal had no effect on the catalytic activity for crystal violet reaction but contributed to total surface area predominantly. Keywords—Copper (I) oxide, Catalytic activity, Crystal violet.
منابع مشابه
Assembly synthesis of Cu2O-on-Cu nanowires with visible-light-enhanced photocatalytic activity.
New Cu2O-on-Cu nanowires (NWs) are constructed to develop the visible-light-driven activity of photocatalysts via the facile self-assembly of Cu2O nanoparticles (NPs) on a Cu NW surface assisted by a structure director, followed in situ reduction. In the resultant Cu2O-on-Cu NWs, the Cu2O NPs, with a diameter of 10 nm, show good distribution on the 50 nm-sized Cu single-crystal NWs. Owing to th...
متن کاملSynthesis of Hierarchical Nanoporous Microstructures via the Kirkendall Effect in Chemical Reduction Process
A series of novel hierarchical nanoporous microstructures have been synthesized through one-step chemical reduction of micron size Cu2O and Co3O4 particles. By controlling the reduction time, non-porous Cu2O microcubes sequentially transform to nanoporous Cu/Cu2O/Cu dented cubic composites and hollow eightling-like Cu microparticles. The mechanism involved in the complex structural evolution is...
متن کاملAn Overview on Platelet-derived Microparticles in Platelet Concentrates: blood collection, method preparation and storage
Preparations of platelet concentrates (PCs) that are stored under blood bank conditions and used for transfusion purposes, appear to be enriched in platelet derived-microparticles (PMPs) with high coagulant activity that may change platelet efficacy and safety issues. High shear stress could cause shedding of PMPs from the platelet plasma membrane, platelet aggregation, and activation of the co...
متن کاملThe Preparation, structural characterization, optical properties, and antibacterial activity of the CuO/Cu2O nanocomposites prepared by the facile thermal decomposition of a new copper precursor
Objective(s): In this study, a new copper precursor was prepared from the combination of Cu(CH3COO)2∙H2O (1 g in 5 ml of methanol) and benzoic acid (1 g in 5 ml of methanol) at room temperature. Following that, the copper precursor was calcined at the temperature of 500ºC and 600ºC for 1.5 hours to form CuO/Cu2O nanocomposites with the code numbers of CuO-1 and CuO-2, respectively. Materi...
متن کاملBinary [Cu2O/MWCNT] and ternary [Cu2O/ZnO/MWCNT] nanocomposites: formation, characterization and catalytic performance in partial ethanol oxidation.
Cuprous oxide agglomerates composed of 4-10 nm Cu2O nanoparticles were deposited on multiwalled carbon nanotubes (MWCNTs) and on ZnO/MWCNTs to give binary [Cu2O/MWCNT] and ternary [Cu2O/ZnO/MWCNT] composites. Di-aqua-bis[2-(methoxyimino)propanoato]copper Cu[O2CCCH3NOMe](2)·2H2O 1 in DMF was used as single source precursor for the deposition of nanoscaled Cu2O. The precursor decomposes either in...
متن کامل