Photoluminescence and photocatalytic properties of rhombohedral CuGaO2 nanoplates.

Rhombohedral phase CuGaO2 nanoplates with a diameter of about 10 μm were synthesized via low temperature hydrothermal method. Room temperature and low temperature photoluminescence of the obtained CuGaO2 nanoplates were characterized. CuGaO2 nanoplates exhibited blue emission at room temperature and free exciton emission were appeared at low temperature. The blue emission is originated from defects such as Cu vacancies, which is the possible origin of p-type conductivity. The appearance of free exciton emission can demonstrate the direct bandgap transition behavior of CuGaO2 nanoplates. The as-prepared p-type CuGaO2 nanoplates were further decorated by n-type ZnO nanoparticles via calcination method to fabricate p-n junction nanocomposites. The nanocomposites exhibited enhanced photocatalytic activity which can be ascribed to the effective separation of photogenerated carriers by the internal electrostatic field in the p-n junction region, and the enhanced light absorption properties resulted from sub-bandgap absorption effect of p-n junction. This work has offered a new insight into the design of p-n junction devices using p-type CuGaO2 nanoplates.