Coercivity enhancement of Nd-Fe-B sintered magnets by grain boundary modification via reduction-diffusion process
نویسندگان
چکیده
The interface between the Nd2Fe14B particles and the grain boundary surrounding them in Nd-Fe-B sintered magnets was modified by diffusion Dy metal selectively through the grain boundary involving the reduction of Dy2O3 or DyF3 with CaH2 and the coercivity of them was effectively enhanced from 0.98 MA/m to 1.42 MA/m with keeping the high value of remanence. The resultant coercivity was higher than that of the magnets modified with Dy2O3 (HcJ = 1.10 MA/m) and DyF3 (HcJ = 1.24 MA/m) without using any reductant such as CaH2, respectively.
منابع مشابه
Relation between domain wall motion and coercivity in Nd-Fe-B sintered magnets prepared in various conditions
For the study of the relationship between the domain wall motion (DWM) and the coercivity in the samples of Dy-free Nd-Fe-B sintered magnets, the DC susceptibility (χDC) in the initial magnetization from the thermally demagnetized state and the DWM in the partially demagnetized state after the full magnetization in 5T-pulse field were measured. In the high coercivity (μ0Hc) samples of μ0Hc=1.35...
متن کاملSintering of Nd-Fe-B Magnets from Dy Coated Powder
High-coercive (Nd,Dy)-Fe-B magnets were fabricated via dysprosium coating on Nd-Fe-B powder. The sputtering coating process of Nd–Fe–B powder yielded samples with densities greater than 98%. (Nd,Dy)2Fe14B phases may have effectively penetrated into the boundaries between neighboring Nd2Fe14B grains during the sputtering coating process, thereby forming a (Nd,Dy)2Fe14B phase at the grain boundar...
متن کاملEffect of Post-Sintering Annealing Treatment on Magnetic Properties of Some Nd Fe b Based Magnets
Effects of post-sintering annealing treatment between 300 and 1000ºC for up to 8 hrs time periods followed by either furnace cooling (FC) or air-cooling (AC) on the hard magnetic properties of some Nd-Fe-B based sintered magnets was investigated. It was shown that the intrinsic coercivity (Hci), second quadrant demagnetization loop shape and thus the energy density (BH)max varied considerably a...
متن کاملModification of the Interface Nanostructure and Magnetic Properties in Nd-Fe-B Thin Films
The effects of Nd2Fe14B grain size and Nd coating on the coercivity in sputter-deposited Nd-Fe-B/Nd thin films have been investigated in order to gain an insight into the coercivity mechanism of Nd-Fe-B magnets. Highly textured Nd2Fe14B particles were grown successfully on the MgO(100) single-crystal substrate with the Mo underlayer. As the Nd-Fe-B layer thickness t NFB was decreased from 70 to...
متن کاملAnalysis Technique for Improving Coercivity of Nd-Fe-B Magnets and Development of Dy-free Magnet
Hiroyuki Yamamoto, Dr. Eng. Isao Kitagawa, Dr. Sc. Teruo Kohashi, Dr. Sc. Akira Sugawara, Dr. Eng. Takeshi Nishiuchi, Dr. Eng. OVERVIEW: Hitachi is working to improve the performance of the NdFe-B magnets that help make people’s way of life more energy efficient and reduce the load it places on the environment. To study the factors that govern coercivity, an important parameter of magnet perfor...
متن کامل