Decreased consumption of Ca and P during in vitro biomineralization and biologically induced deposition of Ni and Cr in presence of stainless steel corrosion products.

The purpose of this study was to investigate the effects of 316L stainless steel (SS) corrosion products on the in vitro biomineralization process, because tissue necrosis, bone loss, impaired bone mineralization, and loosening of orthopedic implants are associated with ions and debris resulting from biodegradation. Rat bone marrow cells were cultured in experimental conditions that favored the proliferation and differentiation of osteoblastic cells and were exposed to SS corrosion products obtained by electrochemical means for periods ranging from 1 to 21 days. Quantification of total and ionized Ca and P, as well as Fe, Cr, and Ni, ions in the culture media of control and metal added cultures during the incubation period was performed to study the influence of corrosion products on the Ca and P consumption that occurs during the mineralization process. Control cultures and metal effects on cultures were evaluated concerning DNA content, enzymatic reduction of 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT), and alkaline phosphatase (ALP) activity. Histochemical detection of ALP, Ca, and phosphate deposition, and examination of the cultures by scanning and transmission electron microscopy (SEM and TEM) were also performed. The presence of SS corrosion products resulted in impairment of the normal behavior of rat bone marrow cultures. Levels of Cr and Ni in the medium of cultures exposed to 316L SS corrosion products decreased throughout the incubation period, suggesting a regular deposition of these species; these results were supported by TEM observation of the cultures. Cultures exposed to the corrosion products presented lower DNA content, MTT reduction, and ALP activity and failed to form mineralized areas. These cultures showed negative staining on histochemical reactions for the identification of calcium and phosphate deposition and SEM and TEM examination did not show mineral globular structures or mineralization foci, respectively, which is characteristic of cultures grown in control conditions. These results suggest that metal ions associated with 316L SS are toxic to osteogenic cells, affecting their proliferation and differentiation.