Synthesis and corrosion protection properties of poly(o-phenylenediamine) nanofibers
نویسندگان
چکیده
The present study shows a novel method for the synthesis of uniformly-shaped poly(othophenylediamine) (PoPD) nanofibers by chemical oxidative polymerization method for application towards smart corrosion resistance coatings. Transmission Electron Microscopy (TEM) and Scanning Electron Microscopy (SEM) studies confirm morphology of PoPD with three dimensional (3D) networked dendritic superstructures having average diameter of 50-70 nm and several hundred meters of length. UV-vis and FTIR spectral results shows the formation of PoPD nanofibers containing phenazine ring ladder-structure with benzenoid and quinoid imine units. Thermogravimetric analyses (TGA) of PoPD nanofibers possess good thermal stability. The anti-corrosion behavior of PoPD nanofibers on 316L SS was investigated in 3.5% NaCl solution using potentiodynamic polarization and electrochemical impedance spectroscopic (EIS) measurements. The PoPD coated 316L SS exhibits higher corrosion potential when compared to uncoated specimen. EIS studies, clearly ascertain that PoPD nanofiber coatings exhibits excellent potential barrier to protect the 316L SS against corrosion in 3.5% NaCl.
منابع مشابه
SYNTHESIS AND STUDY OF CORROSION PERFORMANCE OF EPOXY COATING CONTAINING MULTI-WALLED CARBON NANOTUBE/ POLY ORTHO AMINOPHENOL NANOCOMPOSITE
The epoxy coatings containing multi-walled carbon nanotube/ poly ortho aminophenol nanocomposite were prepared and used as anticorrosive coatings. The nanocomposites with different contents of carbon nanotube were synthesized in a solution of sodium dodecyl sulfate and ammonium peroxy disulfate as a surfactant and an oxidant, respectively. The morphology and structural properties were confirmed...
متن کاملStudying the Corrosion Protection Behavior of an Epoxy Composite Coating Reinforced with Functionalized Graphene Oxide by Second and Fourth Generations of Poly(amidoamine) Dendrimers (GO-PAMAM-2, 4)
In this research, graphene oxide (GO) nanoparticles were modified by second and fourth generations of poly(amidoamine) dendrimers in order to improve the particle dispersion quality in the epoxy matrix and therefore its barrier anti-corrosion performance. Confirmation on the GO surface modification by Polyamidoamine generation 2 (PAMAM2) and polyamidoamin generation 4 (PAMAM4) was carried o...
متن کامل5-sulfosalicylic acid as an efficient organocatalyst for environmentally benign synthesis of 2-substituted benzimidazoles
A water soluble, Bronsted acid, 5-sulfosalicylic acid as an efficient organocatalyst was used for the synthesis of physiologically active 2-substituted benzimidazole derivatives from o-phenylenediamine and aromatic aldehydes in ethanol at reflux condition. Cost-effectiveness, use of non-hazardous solvents, metal free and commercially available catalyst, single-step, environmentally fri...
متن کاملInvestigation of corrosion protection properties of TiO2-CdO nanocomposite coating prepared by sol-gel method on copper
the Sol–gel nanocomposite coatings have been investigated for copper metal as a potential replacement for the hazardous and banned hexavalent chromate conversion coatings. TiO2–CdO nanocomposite thin films were deposited on copper using the sol–gel method. The sol-gel coatings were prepared using a sol obtained by the hydrolysis and condensation of tetra-o-butyl titanate. They were doped with c...
متن کاملSYNTHESIS AND CORROSION PROTECTION BEHAVIOR OF EPOXYTiO2-MICACEOUS IRON OXIDE NANO - COMPOSITE COATING ON St-37
The micro layers micaceous iron oxide and nano-TiO 2 were incorporated into the epoxy resin by mechanical mixing and sonication process. Optical micrographs showed that the number and diameter size of nanoparticle agglomerates were decreased by sonication. The structure and composition of the nanocomposite was determined using transmission electron microscopy which showed the presence of disper...
متن کامل