Low Thermal Budget NiSi Films on SiGe Alloys
نویسندگان
چکیده
Nickel silicides were formed on Si (100) substrates and CVD grown Si0.9Ge0.1/Si layers by low thermal budget annealing of evaporated Ni films to evaluate their utility for ultra shallow junctions. The phase formation and microstructure of silicides formed using conventional furnace and rapid thermal annealing were studied by x-ray diffraction, Rutherford backscattering (RBS), x-ray photoelectron spectroscopy (XPS) and atomic force microscopy. RBS simulations and XPS study revealed the formation of a ternary nickel germanosilicide phase for the SiGe alloy. The incorporation of Ge resulted in a higher temperature window for the stability of lowresistive monosilicide phase. Electrical properties of the grown silicides were characterized by four-probe resistivity and contact resistance measurements.
منابع مشابه
Enhanced in-plane thermoelectric figure of merit in p-type SiGe thin films by nanograin boundaries.
P-Type polycrystalline silicon-germanium (SiGe) thin films are grown by low-pressure chemical vapor deposition (LPCVD) and their thermoelectric properties are characterized from 120 K to 300 K for potential application in integrated microscale cooling. The naturally formed grain boundaries are found to play a crucial role in determining both the charge and thermal transport properties of the fi...
متن کاملImproved Thermal Stability of NiSi Nanolayer in Ni-Si Co-sputtered Structure
Electrical, structural and morphological properties of Ni silicide films formed in Ni(Pt 4at.% )/Si(100) and Ni0.6Si0.4(Pt4at.% )/Si(100) structures at various annealing temperatures ranging from 200 to 1000 oC were studied. The Ni(Pt) and Ni0.6Si0.4(Pt) films with thickness of 15 and 25 nm were deposited by RF magnetron co-sputtering method, respectively. The annealing process of the structur...
متن کاملStrained-Si heterostructure field effect transistors
The purpose of this review article is to report on the recent developments and the performance level achieved in the strained-Si/SiGe material system. In the first part, the technology of the growth of a high-quality strained-Si layer on a relaxed, linear or step-graded SiGe buffer layer is reviewed. Characterization results of strained-Si films obtained with secondary ion mass spectroscopy, Ru...
متن کاملThermal conductivity of SiÕSiGe superlattice nanowires
The thermal conductivities of individual single crystalline Si/SiGe superlattice nanowires with diameters of 58 and 83 nm were measured over a temperature range from 20 to 320 K. The observed thermal conductivity shows similar temperature dependence as that of two-dimensional Si/SiGe superlattice films. Comparison with the thermal conductivity data of intrinsic Si nanowires suggests that alloy ...
متن کاملAbsorption Amelioration of Amorphous Si Film by Introducing Metal Silicide Nanoparticles
Amorphous Si (a-Si) films with metal silicide are expected to enhance the absorption ability of pure a-Si films. In this present study, NiSi (20 nm)/Si (40 nm) and AlSi (20 nm)/Si (40 nm) bilayer thin films are deposited through radio frequency (RF) sputtering at room temperature. The influence of the film's composition and the annealing temperature on the film's optical absorption is investiga...
متن کامل