Inhibition Effect of 2,2’-bipyridyl on the Corrosion of Austenitic Stainless Steel in 0.5M H2SO4
نویسنده
چکیده
The corrosion inhibition of AISI309 austenitic stainless steel by 2,2'-Bipyridyl in 0.5M H 2 SO 4 at 298K was studied using the mass loss’ method, the potentiodynamic polarization (Tafel), the linear polarization (LRP) and the electrochemical impedance spectroscopy (EIS). The results showed a mixed inhibition mode and an increase in the charge transfer resistance, due to inhibitor molecules’ adsorption at steel surface. This latter obeys to Langmuir isotherm. The observation by scanning electron microscopy (SEM) and the analysis by energy dispersion spectrometry (EDS) confirm an inhibitor film’s presence. The calculated inhibition efficiencies are in accordance with 87.78% maximum value. Keyword: AISI309, 2,2'-Bipyridyl, Corrosion; Inhibition, EIS, Tafel.
منابع مشابه
The Inhibition Effect of Polyethylenimine (PEI) on Pitting Corrosion of 304 Austenitic Stainless Steel in 3.5% NaCl Solution
One of the problems in the case of stainless steels is their low corrosion resistance against pitting corrosion in chloride containing environments, thereby leading to severe damage to industries. In this research, the pitting corrosion of 304 austenitic stainless steel was studied in 3.5% NaCl solution at room temperature (25˚C) by performing electrochemical measurements (containing cyclic pol...
متن کاملInvestigation of the Effect of Vanillin as a Green Corrosion Inhibitor for Stainless Steel Using Electrochemical Techniques
Vanillin offers interesting possibilities for corrosion inhibition because of its safe use and highsolubility in water. The effect of vanillin on the corrosion inhibition of AISI 304 stainless steel in0.5M H2SO4 solution has been studied using potentiodynamic polarization and electrochemicalimpedance spectroscopy (EIS). Furthermore, this paper demonstrates that the electrochemical noise(EN) tec...
متن کاملA Corrosion Study of Grain-Refined 304L Stainless Steels Produced by the Martensitic Process
AISI 304L austenitic stainless steel with different grain sizes of 0.5 -12 μm was obtained through the martensitic process. Corrosion behavior of different samples was investigated in a 0.5M HCl solution using open circuit potential, potentiodynamic polarization and electrochemical impedance spectroscopy tests. Also, the correlation between the grain size and pitting corrosion resistance was as...
متن کاملStudy of the Corrosion Resistance of Type 304L and 316 Austenitic Stainless Steels in Acid Chloride Solution
The corrosion resistance of type 304L and 316 austenitic stainless steels in 2M H2SO4 at 0-1.5%NaCl concentrations was studied through potentiodynamic polarization technique and optical microscopy analysis. The corrosion rate, pitting potential, passivation potential and surface morphology of both steel where significantly altered by the Clion concentration, alloy composition and metallurgical ...
متن کاملThe Evaluation of Corrosion Behavior of AISI 347 Stainless Steel to ASTM A335 Low Alloy Steel Dissimilar Welds
In the present study, the corrosion behavior of AISI 347 austenitic stainless steel to ASTM A335 low alloy steel dissimilar joint was investigated. For this purpose, two filler metals, ER309L and ERNiCr-3, were selected to be used during the gas tungsten arc welding process. To investigate the corrosion behavior of the joints after welding, the specimens were tested in 3.5% sodium chloride solu...
متن کامل