Objective: Human jawbones consist mainly of hydroxylapatite. The aim of this study was to assess the structure of solid calcium phosphate compounds of the jaw bone (JB) in cases of normal and osteoporotic JBs. Design: The X-ray diffraction technique was used to analyze the structure of samples of cadavers’ jawbones. The experimental JB samples were taken from an osteoporotic and atrophic jawbone, and control samples were from normal and nonosteoporotic bone samples. Results: Hydroxylapatite was the only phase in control bone samples. In experimental bone samples, the above-mentioned phase was registered, as well as monetite and brushite. Conclusion: The obtained data indicated that the changes of crystalographic forms of calcium phosphate in the physiologic system were balanced according to the possibility of change in the inorganic chemical system.
منابع مشابه
Enhancing the bioactivity of a calcium phosphate glass-ceramic with controlled heat treatment
In this paper synthesis and characterization of a bioactive calcium phosphate glass-ceramic is presented, synthesized using a facile method. The glass-ceramic samples are synthesized with heat treating the parent glass at appropriate temperatures, where different calcium phosphate crystalline phases are grown in the parent glass samples during the heat treatment. The amounts of elements a...
متن کاملInvestigation of the effect of phosphate on the physical and microstructural properties of synthetic calcium aluminate cement
The aim of this study was to investigate the synthesis of calcium aluminate cement with and without phosphate additive by combustion synthesis. After preparing the gel from a solution containing aluminum and calcium nitrates and glycine fuel and ammonium dihydrogen Phosphate, its combustion was performed at 400 ° C. X-ray diffraction pattern and thermal analysis of the combustion sample showed...
متن کاملTime-resolved in situ studies of apatite formation in aqueous solutions
Formation of hydroxylapatite through the precipitation and evolution of calcium phosphate precursor phases under varying conditions of temperature (25–90 °C), pH (6.5–9.0), and calcium to phosphorus ratio (1.0, 1.33, 1.5, and 1.67) comparable to those found in many sediments and soils were studied. The products of low-temperature precipitation were analyzed by ex situ X-ray diffraction and SEM,...
متن کاملگرمای ویژه و پذیرفتاری الکتریکی لایههای نازک فروالکتریک
The phase formation and solid solid solution system of Lithium Iron (II) Phosphate and Lithium Manganese (II) Phosphate using solid state reaction have been studied. The observed phases were identified by X-ray powder diffraction and Electrochemical measurements. The synthesised phases show X-ray diffraction spectra typical of orthorhombic symmetry, space group Pmnb and are closely related to ...
متن کاملA New Mixture of Nano-structure of Potassium-incorporated Hydroxyapatite/β-tricalcium Phosphate/calcium Pyrophosphate
The new triphasic potassium−substituted hydroxyapatite (KHAP), β−tricalcium phosphate (β−TCP), and calcium pyrophosphate (CPP) proportions using easy sol−gel method were synthesized. The prepared powders was characterized by X–ray diffraction (XRD), Fourier transform infrared (FTIR), Differential thermal behavior (DTA) analysis, Energy Dispersive X–ray Analysis (EDXA), and Brunauer–Emmett–Telle...
متن کامل