Pitting Corrosion of Metals A Review of the Critical Factors
نویسنده
چکیده
Pitting corrosion is localized accelerated dissolution of metal that occurs as a result of a breakdown of the otherwise protective passive film on the metal surface. This paper provides an overview of the critical factors influencing the pitting corrosion of metals. The phenomenology of pitting corrosion is discussed, including the effects of alloy composition, environment, potential, and temperature. A summary is then given of studies that have focused on various stages of the pitting process, including breakdown of the passive film, metastable pitting, and pit
منابع مشابه
Probability Approach for Prediction of Pitting Corrosion Fatigue Life of Custom 450 Steel
In this study, the pitting type of corrosion growth characteristics, fatigue crack initiation and propagation behavior; axial fatigue tests were carried out on precipitation hardened martensitic Custom 450 steel in the air and 3.5wt% NaCl solution. Using the ratio of the depth to the half-width of the pits; (a/c)= 1.5±0.2 the corrosion pit depth growth law was obtained as a function of stress a...
متن کاملDETERIORATION OF PITTING CORROSION OF 316 STAINLESS STEEL BY SENSITIZATION HEAT TREATMENT
In this research pitting Corrosion of a sensitized 316 stainless steel was investigated employing potentiodynamic, potentiostatic techniques. Sensitization process was carried out on as-received alloy by submitting the specimen in electric furnace set at 650°Cfor five hours and then the specimen was quenched 25°C water. Potentiodynamic polarization of as received and sensitized specimens in 1M ...
متن کاملStress- Corrosion Crack Initiation of High-strength Pipeline Steel in Near-neutral pH Environments
Stress-corrosion cracking (SCC) tests were conducted in the near-neutral pH standard solution, NS4, and in an actual soil solution, using four-point bending at a high stress ratio and low frequency conditions very similar to those of operational pipelines. Pitting incubation appeared first and then pitting initiated and grew in both solutions although there were many more pits on the specimen t...
متن کاملThe Inhibition Effect of Polyethylenimine (PEI) on Pitting Corrosion of 304 Austenitic Stainless Steel in 3.5% NaCl Solution
One of the problems in the case of stainless steels is their low corrosion resistance against pitting corrosion in chloride containing environments, thereby leading to severe damage to industries. In this research, the pitting corrosion of 304 austenitic stainless steel was studied in 3.5% NaCl solution at room temperature (25˚C) by performing electrochemical measurements (containing cyclic pol...
متن کاملStatistical Approach on Corrosion Behavior of Dissimilar Welds of A387-Gr91/AISI316 Steels with PCGTAW Process
In this study, an attempt was made to minimize the corrosion rate and maximize pitting potential of dissimilar metal welded joints of A387-Gr91/AISI316 steels. Process parameters of the pulsed current gas tungsten arc welding (PCGTAW) including of peak current (P), background current (B), pulse frequency (F), and on time percentage (O) were chosen as the influencing factors on corrosion behavio...
متن کامل