Fabrication of Corrosion Resistance Micro-Nanostructured Superhydrophobic Anodized Aluminum in a One-Step Electrodeposition Process
نویسندگان
چکیده
The formation of low surface energy hybrid organic-inorganic micro-nanostructured zinc stearate electrodeposit transformed the anodic aluminum oxide (AAO) surface to superhydrophobic, having a water contact angle of 160 ̋. The corrosion current densities of the anodized and aluminum alloy surfaces are found to be 200 and 400 nA/cm2, respectively. In comparison, superhydrophobic anodic aluminum oxide (SHAAO) shows a much lower value of 88 nA/cm2. Similarly, the charge transfer resistance, Rct, measured by electrochemical impedance spectroscopy shows that the SHAAO substrate was found to be 200-times larger than the as-received aluminum alloy substrate. These results proved that the superhydrophobic surfaces created on the anodized surface significantly improved the corrosion resistance property of the aluminum alloy.
منابع مشابه
Corrosion Resistance Improvement of Aluminum by Hydrophobic Anodic Oxide Film
Diminishing surface wettability is an effective method to improve corrosion resistance of aluminum. Various techniques for preparing hydrophobic surface have been reported, most of which use organic coating as the final step. The key point to diminish surface wettability is to form a fine regular surface structure, and the porous type anodic oxide film (PAOF) has nano-pore structure, therefore ...
متن کاملRobust superhydrophobic surface on Al substrate with durability, corrosion resistance and ice-phobicity
Practical application of superhydrophobic surfaces is limited by the fragility of nanoscale asperities. Combining chemical etching and anodization, microscale pits and nanoscale pores, instead of the micro and nano protrusions on traditional superhydrophobic surfaces mimicking Lutos leaves, were fabricated on commercially pure aluminum surfaces. After modified by FDTS, the surfaces were superhy...
متن کاملGrowth and Characterization of Iron Nanowires Into Anodized Aluminum Oxide Templates Using Electrodeposition Technique
The Fe nanowires were prepared by Ac electrodeposition method. The two steps anodized aluminum oxides (alumina) were used as templates for electrodeposition of magnetic nanowires. Sulfuric acid was used to anodize aluminum. The pours diameter and growth rate of alumina were investigated. The FeSO4 electrolyte was used for growth of nanowires. The prepared magnetic nanowires were characterized b...
متن کاملOptimization of the FeCo nanowire fabrication embedded in anodic aluminum oxide template by response surface methodology
Anodic aluminum oxide (AAO) fabricated by two step anodization technique, is used as a template to synthesize FeCo nanowire arrays by AC electrodeposition technique. Response surface methodology (RSM) is applied to design the experiments, fit an empirical model and optimize the conditions to achieve the best magnetic properties. The magnetic properties, pore dimensions, composition and structur...
متن کاملA Rapid One-Step Process for Fabrication of Biomimetic Superhydrophobic Surfaces by Pulse Electrodeposition
Inspired by some typical plants such as lotus leaves, superhydrophobic surfaces are commonly prepared by a combination of low surface energy materials and hierarchical micro/nano structures. In this work, superhydrophobic surfaces on copper substrates were prepared by a rapid, facile one-step pulse electrodepositing process, with different duty ratios in an electrolyte containing lanthanum chlo...
متن کامل