Effect of Abrasive Particle Size on Abrasive Wear Resistance in Otomotive Steels
نویسنده
چکیده
If one of the surfaces which are in touch is rough and hard, it chips the other surface due to relative motion or touching forces. The wear is called two-body abrasive wear. If there are free abrasive particles between the two bodies, the wear is called three-body abrasive wear. The free abrasive particles may be external material dust or the remains of chipping. Usually, the wear starts as a two-body abrasive or adhesive wear and then becomes a threebody wear as dust form between the two surfaces due to external particles, chipping remains, or oxide particles. In three-body abrasive wear, wear rate increases as diameter of abrasive particles increases. Gouging, high stress abrasion and low stress abrasion are types of three-body abrasive wear [1-3].
منابع مشابه
Effect of Carbide Particle Size on the Microstructure, Mechanical properties, and Wear Behavior of HVOF-sprayed WC-17% Co Coatings
This study investigates the effect of carbide particle size on the microstructure, mechanical properties, and abrasive wear resistance of WC-17%Co HVOF-sprayed coatings. The characteristics of WC-1, WC-2, and WC-3 coatings with carbide sizes of 1 µm, 0.9 µm, and 0.5 µm, respectively, were also investigated. WC-1 coating experienced the maximum carbon loss of 42%, while WC-2 and WC-3 coatings un...
متن کاملThe Effect to Epsilon Phase on the Friction and Wear of Nitrided Die Steels (RESEARCH NOTE)
In this paper, the wear resistance and antifriction of epsilon phase layer and diffusion layer of gas nitrided D2 steel and M2 steel have been studied. The changes m wear mechanism of epsilon phase under the load from 20N to 200N are analysed. When the load is lighter than 100N, it is mainly oxidizing wear on friction surface. The adhesion, peeling off and abrasive wear appear on friction surfa...
متن کاملTHE EFFECT OF HEAT TREATMENT ON ABRASIVE WEAR RESISTANCE OF Fe-34Cr-4.5C%WT HARDFACING ALLOY
Abstract: Hardfacing is one of the most useful and economical ways to increase the service life of components subjected to abrasive wear. Iron based hardfacing alloys have long been considered as candidate coatings for wear-resistant applications in industry. In the present work two layer of Fe-34Cr-4.5C%wt hardfacing alloy was deposited on ASTM A36 carbon steel plates by SMAW method. The m...
متن کاملAN INVESTIGATION ON ABRASIVE WEAR BEHAVIOUR OF Fe-C-Mo-FeCr COMPOSITE PRODUCED BY POWDER METALLURGY
In this study, the effect of chromium carbide (Cr7C3) on abrasive wear behavior of Fe-C-Mo-FeCr composite was investigated. Composite, which was produced by a powder metallurgy route was containing 3 wt.% Mo, 1.5 wt. % C and 4,8,12 wt. % FeCr with the different particle sizes. In the experiments, wear resistance of samples were determined using different loads by a pin on disc wear tester. Micr...
متن کاملModeling and Predicting Abrasive Wear Behaviour of Poly Oxy Methylenes Using Response Surface Methodolgy and Neural Networks
Abrasive wear is defined wear due to hard particles or hard protuberances forced againts and moving along a solid surface. This defination encompasses several different mechanisms by which material removal occoures. The five types of wear are abrasive, adhesive, erosion, fatigue and fretting. The abrasive wear of polymeric materials is the interest and the subject of quite number of literature....