Evidence for the transition from primary to peritectic phase growth during solidification of undercooled Ni-Zr alloy levitated by electromagnetic field

نویسندگان

  • P. Lü
  • K. Zhou
  • H. P. Wang
چکیده

The Ni83.25Zr16.75 peritectic alloy was undercooled by electromagnetic levitation method up to 198 K. The measured dendritic growth velocity shows a steep acceleration at a critical undercooling of ΔTcrit = 124 K, which provides an evidence of the transition of the primary growth mode from Ni7Zr2 phase to peritectic phase Ni5Zr. This is ascertained by combining the temperature-time profile and the evolution of the solidified microstructures. Below the critical undercooling, the solidified microstructure is composed of coarse Ni7Zr2 dendrites, peritectic phase Ni5Zr and eutectic structure. However, beyond the critical undercooling, only a small amount of Ni7Zr2 phase appears in the solidified microstructure. The dendritic growth mechanism of Ni7Zr2 phase is mainly governed by solute diffusion. While, the dendritic growth mechanism of Ni5Zr phase is mainly controlled by thermal diffusion and liquid-solid interface atomic attachment kinetics.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Dendritic solidification and fragmentation in undercooled Ni–Zr alloys

Kinetics of dendritic solidification and fragmentation of dendritic crystals in undercooled Ni–Zr samples are studied. Using the capacitance roximity sensor technique and a high-speed-camera system, the dendrite growth velocity has been measured as a function of initial undercooling n solidifying droplets processed by the electromagnetic levitation technique. Analyses of solidified droplets giv...

متن کامل

Dendrite Growth Kinetics in Undercooled Melts of Intermetallic Compounds

Solidification needs an undercooling to drive the solidification front. If large undercoolings are achieved, metastable solid materials are solidified from the undercooled melt. Containerless processing provides the conditions to achieve large undercoolings since heterogeneous nucleation on container walls is completely avoided. In the present contribution both electromagnetic and electrostatic...

متن کامل

Direct formation of peritectic phase but no primary phase appearance within Ni83.25Zr16.75 peritectic alloy during free fall

Ni83.25Zr16.75 peritectic alloy was containerlessly solidified in a drop tube. When the droplet diameter exceeds a critical value (Dcrit), Ni7Zr2 phase primarily solidifies, followed by the peritectic reaction of Ni7Zr2 + L → Ni5Zr. Once the droplet diameter is smaller than the critical value (Dcrit), peritectic phase Ni5Zr directly solidifies from the undercooled melt by completely suppressing...

متن کامل

Effect of a weak transverse magnetic field on the microstructure in directionally solidified peritectic alloys

Effect of a weak transverse magnetic field on the microstructures in directionally solidified Fe-Ni and Pb-Bi peritectic alloys has been investigated experimentally. The results indicate that the magnetic field can induce the formation of banded and island-like structures and refine the primary phase in peritectic alloys. The above results are enhanced with increasing magnetic field. Furthermor...

متن کامل

Detachment of secondary dendrite arm in a directionally solidified Sn-Ni peritectic alloy under deceleration growth condition

In order to better understand the detachment mechanism of secondary dendrite arm during peritectic solidification, the detachment of secondary dendrite arm from the primary dendrite arms in directionally solidified Sn-36at.%Ni peritectic alloys is investigated at different deceleration rates. Extensive detachment of secondary dendrite arms from primary stem is observed below peritectic reaction...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 6  شماره 

صفحات  -

تاریخ انتشار 2016