Fast and highly efficient SO2 capture by TMG immobilized on hierarchical micro-meso-macroporous AlPO-5/cordierite honeycomb ceramic materials.
نویسندگان
چکیده
SO2 capacity of the obtained TMG-AlPO-5/cordierite honeycomb ceramic (CHC) adsorbent was measured to be 1.13 mol per mol TMG. More importantly, compared with literature reported supported ionic liquids, it is featured by a significantly improved adsorption rate (t0.9 reduced from >30 min to ∼0.1 min) and negligible pressure drop.
منابع مشابه
Poisoning Effect of SO2 on Honeycomb Cordierite- Based Mn–Ce/Al2O3Catalysts for NO Reduction with NH3 at Low Temperature
Honeycomb cordierite-based Mn–Ce/Al2O3 catalysts were prepared by the impregnation method and used for low-temperature selective catalytic reduction (SCR) of NOx with NH3, with and without SO2 and/or H2O in a homemade fixed-bed tubular reactor. The catalyst reached nearly 80% NOx conversion at 100 ◦C in the absence of SO2. However, SO2 reduces the catalytic activity (80% to 72%) of the honeycom...
متن کاملImmobilization of Glucose oxidase on Meso-porous Glass-ceramic with the Skeleton of CaTi4(PO¬4)6
Microporous glass ceramic with skeleton of CaTi4(PO¬4)6 with average pore size of 12.7 nm has been synthesized and used as a carrier of glucose oxidase. The glass ceramic was prepared by controlled heat treatment of glass samples, which causes the phase separation in their structure and creates CaTi4(PO¬4)6 and β-Ca3(PO4)2 phases. The β-Ca3(PO4)2 phase was dissolved by soaking the glass ceramic...
متن کاملEffect of milling time and microwave sintering on microhardness and electrical properties of nano and micro structured cordierite
The purpose of this research is to investigate the mechanical and electrical properties of nano structured cordierite. Nano grain size powders were synthesized through mechanical activation by high-energy ball milling of the starting powders containing 34.86 wt% Al2O3, 51.36 wt% SiO2, and 13.78 wt% MgO. Samples were prepared by conventional and microwave sintering at 1390°C. SEM observations il...
متن کاملA Hierarchically Micro-Meso-Macroporous Zeolite CaA for Methanol Conversion to Dimethyl Ether
A hierarchical zeolite CaA with microporous, mesoporous and macroporous structure was hydrothermally synthesized by a ”Bond-Blocking” method using organo-functionalized mesoporous silica (MS) as a silica source. The characterization by XRD, SEM/TEM and N2 adsorption/desorption techniques showed that the prepared material had well-crystalline zeolite Linde Type A (LTA) topological structure, mic...
متن کاملAn Optimum Routine for Surface Modification of Ceramic Supports to Facilitate Deposition of Defect-Free Overlaying Micro and Meso (Nano) Porous Membrane
In this work, a simple and effective way to modify the support surface is developed and a nanostructure ceramic support to facilitate deposition of a defect-free overlying micro and meso (nano) porous membrane is obtained. To achieve high performance nanocomposite membranes, average pore size of outer surface of support was reduced by dip-coating in submicron and nano α-alumina slurries. In...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 52 38 شماره
صفحات -
تاریخ انتشار 2016