Field emission from in situ-grown vertically aligned SnO2 nanowire arrays
نویسندگان
چکیده
Vertically aligned SnO2 nanowire arrays have been in situ fabricated on a silicon substrate via thermal evaporation method in the presence of a Pt catalyst. The field emission properties of the SnO2 nanowire arrays have been investigated. Low turn-on fields of 1.6 to 2.8 V/μm were obtained at anode-cathode separations of 100 to 200 μm. The current density fluctuation was lower than 5% during a 120-min stability test measured at a fixed applied electric field of 5 V/μm. The favorable field-emission performance indicates that the fabricated SnO2 nanowire arrays are promising candidates as field emitters.
منابع مشابه
Patterned growth of carbon nanotubes over vertically aligned silicon nanowire bundles for achieving uniform field emission
A fabrication strategy is proposed to enable precise coverage of as-grown carbon nanotube (CNT) mats atop vertically aligned silicon nanowire (VA-SiNW) bundles in order to realize a uniform bundle array of CNT-SiNW heterojunctions over a large sample area. No obvious electrical degradation of as-fabricated SiNWs is observed according to the measured current-voltage characteristic of a two-termi...
متن کاملEnhanced electron field emission properties of high aspect ratio silicon nanowire-zinc oxide core-shell arrays.
The enhanced electron field emission (EFE) properties of high aspect ratio, vertically aligned SiNW-ZnO core-shell arrays are presented. These core-shell arrays are prepared by a thin, controlled, highly crystalline and conformal coating of zinc oxide as shell using the plasma assisted-atomic layer deposition (PA-ALD) route on vertically aligned silicon nanowire arrays core. The core-shell nano...
متن کاملSynthesis, characterization and electrical properties of hybrid Zn2GeO4–ZnO beaded nanowire arrays
We report the syntheses of vertically aligned, beaded zinc germinate (Zn2GeO4)/zinc oxide (ZnO) hybrid nanowire arrays via a catalyst-free approach. Vertically aligned ZnO nanowire is used as a lattice matching reactive template for the growth of Zn2GeO4/ZnO nanowire. The morphology and structure of the as-prepared samples were characterized using X-ray diffractometry (XRD), scanning electron (...
متن کاملDense and vertically-aligned centimetre-long ZnS nanowire arrays: ionic liquid assisted synthesis and their field emission properties.
Based on the self-ordering behavior of ionic liquids on solid surface, a gold ion containing ionic liquid was employed to obtain a uniform pattern of gold nanoparticles on Si substrate. Using this catalytic pattern, super-dense, centimetre long, well-crystallized and vertically-aligned ZnS nanowire arrays were then generated. It was found that the densely-packed gold nanoparticles played a key ...
متن کاملReshaping the Tips of ZnO Nanowires by Pulsed Laser Irradiation
Vertically aligned ZnO nanowires have been synthesized by a hydrothermal method. After being irradiated by a short laser pulse, the tips of the as-synthesized ZnO nanowires can be tailored into a spherical shape. Transmission electron microscopy revealed that the spherical tip is a single-crystalline piece connected to the body of the ZnO nanowire, and that the center of the sphere is hollow. T...
متن کامل