The Microstructural Evolution of Vacuum Brazed 1Cr18Ni9Ti Using Various Filler Metals
نویسندگان
چکیده
The microstructures and weldability of a brazed joint of 1Cr18Ni9Ti austenitic stainless steel with BNi-2, BNi82CrSiBFe and BMn50NiCuCrCo filler metals in vacuum were investigated. It can be observed that an interdiffusion region existed between the filler metal and the base metal for the brazed joint of Ni-based filler metals. The width of the interdiffusion region was about 10 μm, and the microstructure of the brazed joint of BNi-2 filler metal was dense and free of obvious defects. In the case of the brazed joint of BMn50NiCuCrCo filler metal, there were pits, pores and crack defects in the brazing joint due to insufficient wettability of the filler metal. Crack defects can also be observed in the brazed joint of BNi82CrSiBFe filler metal. Compared with BMn50NiCuCrCo and BNi82CrSiBFe filler metals, BNi-2 filler metal is the best material for 1Cr18Ni9Ti austenitic stainless steel vacuum brazing because of its distinct weldability.
منابع مشابه
An investigation on metallurgical and mechanical properties of vacuum brazed Ti-6Al-4V to 316L stainless steel using Zr-based filler metal
Both Ti-6Al-4V and 316L stainless steels are widely used as engineering alloys. Fusion welding of these two alloys is not easily possible due to their incomplete solubility in each other. Brazing is one of the best choices for joining dissimilar alloys. In this study, wettability experiments were done at 940 and 970 ºC for 5, 15 and 30 min. Also, joining of these two alloys was carried out at 9...
متن کاملDevelopment of dissimilar GTA 4130/201 SS weld joint and investigation on the effect of filler metals in order to obtain improved mechanical properties and microstructural features
In this research, gas tungsten arc welding of dissimilar joint between 4130 low alloy steel and AISI 201 austenitic stainless steel was investigated. Four filler metals i. e. ERNiCr-3, ER 309L, ER 308L and ER 80SB2 were used. After welding, microstructural features of various areas and also fracture surfaces were examined using optical microscopy and scanning electron microscopy. Tensile test w...
متن کاملDevelopment of dissimilar GTA 4130/201 SS weld joint and investigation on the effect of filler metals in order to obtain improved mechanical properties and microstructural features
In this research, gas tungsten arc welding of dissimilar joint between 4130 low alloy steel and AISI 201 austenitic stainless steel was investigated. Four filler metals i. e. ERNiCr-3, ER 309L, ER 308L and ER 80SB2 were used. After welding, microstructural features of various areas and also fracture surfaces were examined using optical microscopy and scanning electron microscopy. Tensile test w...
متن کاملBrazing & Soldering Today
Brazed components play an essential role in consistent joining techniques. The brazing process is characterized by low process temperatures and fast processing times, compared to welding techniques. Beside the resulting low manufacturing costs, brazing can join dissimilar materials, e.g. metals and ceramics. Consequently, brazing provides potential for many industrial applications like the prod...
متن کاملWelding of 304L Stainless Steel to 409 Stainless Steel with GMAW Process Using ER316LSi and ER309LMo Filler Metals
Dissimilar welding of AISI 304L austenitic stainless steel to AISI 409 ferritic stainless steel with GMAW process usingtwo Ar-O2 and Ar-CO2 shielding gas mixtures was studied. ER316LSi and ER309LMo filler metals were chosen by considering 5 and 15% delta ferrite according to the Schaeffler equations and diagram. Based on the observations, both filler metals accompanied by Ar-2%O2 shielding gas ...
متن کامل