Role of process parameters on bondability and pad damage indicators in copper ball bonding

نویسندگان

  • I. Qin
  • A. Shah
  • C. Huynh
  • M. Meyer
  • M. Mayer
  • Y. Zhou
چکیده

Cu wire bonding is one of the hottest trends in electronic packaging due to the cost and performance advantages of Cu wire over Au wire. However, there are many challenges to Cu wire bonding, one of which is the increased stress transmitted to the bond pad during bonding. This high stress is not desirable as it leads to pad damage or cratering in the Si under the pad. Another issue is pad splash in which the pad material is squeezed outside the bonded area, which in severe cases can cause Al pad thinning and depletion. To study the root cause of the increased stress, ball bonding is performed with Au and Cu wires using the same levels of ultrasound (USG), bonding force (BF), and impact force (IF). The bonding is performed on a bonding test pad with integrated piezoresistive microsensors and the in situ pad stress is measured in real time. The ultrasonic pad stress did not show any significant difference between the Au and the Cu ball bonding processes. This indicates that the cause of increased stress cannot be attributed to material properties such as hardness alone, and that the differences in bondability and bonding parameters required for the Cu process might be more influential. To achieve optimal bonding results in terms of shear force per unit area, the Cu process requires higher BF and USG settings, which are the main causes of pad damage. To understand the effect of bonding parameters IF, BF, and USG on pad stress, a detailed DOE is conducted with Cu wire. In addition to conventional bonding parameters, the effect of a non-zero USG level applied during the impact portion of the bonding (pre-bleed USG) is investigated. One of the findings is the reduction of pad damage when higher pre-bleed USG levels are used. 2010 Elsevier Ltd. All rights reserved.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Wire Bonding to Advanced Copper, Low-K Integrated Circuits, the Metal/Dielectric Stacks, and Materials Considerations

There are three areas to consider when designing/implementing wire bonding to advanced ULSI damascene–copper chips having copper metallization and low dielectric-constant polymers embedded beneath them (Cu/LoK). These are: 1) the copper-pad top-surface oxidation inhibitor coatingmetal/organic/inorganic. (Current work involves evaluating the metal and inorganic options); 2) the low dielectric co...

متن کامل

Next Generation Nickel-Based Bond Pads Enable Copper Wire Bonding

Copper wire bonding has huge cost advantages over gold wire bonding. As a result, low pin count, heavy wire applications have already been converted to copper wire and many companies are in high volume production. Recently, with the price of gold skyrocketing, conversion of high pin count (>250 I/O), high performance applications to Cu has dramatically accelerated. These high performance device...

متن کامل

Role of impact ultrasound on bond strength and Al pad splash in Cu wire bonding

Cu wire is replacing Au wire in the microelectronic industry due to its lower cost. However, during Cu ball bonding one of the main challenges is the increased stress that can damage the pad and underpad layers. Past work showed that using ultrasound superimposed together with impact force (pre-ultrasound) results not only in a softer bonded ball, but also in a flatter ball/pad interface. In th...

متن کامل

The Effect of Ultrasonic Frequency on Gold Wire Bondability and Reliability

�This paper presents a systematic study on the effect of 120 KHz ultrasonic frequency on the bondability and reliabili­ ty of fine pitch gold wire bonding to pads over an organic sub­ strate with gold metallizations. The study was carried out on a thermosonic ball bonder that is allowed to easily switch between ultrasonic frequencies of 60 KHz and 120 KHz by changing the ultrasonic transducer a...

متن کامل

Two capillary solutions for ultra-fine-pitch wire bonding and insulated wire bonding

In this article, the new challenges and requirements in wire bonding are discussed, the problems in ultra-fine-pitch wire bonding and insulated wire bonding are analyzed, and then two capillary solutions to the problems are presented. Actual bonding experiments using the new capillaries were carried out and the results were satisfactory. Compared to the standard design, a new capillary design h...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Microelectronics Reliability

دوره 51  شماره 

صفحات  -

تاریخ انتشار 2011