Effect of Y Addition on the Microstructure and Mechanical Properties of Sn-Zn Eutectic Alloy
نویسندگان
چکیده
The effect of Yttrium addition on the microstructure and mechanical properties of Sn-Zn eutectic alloy, which has been attracting intensive focus as a Pb-free solder material, was investigated in this study. Phase equilibrium has been calculated by using FactSage® to evaluate the composition and fraction of equilibrium intermetallic compounds and construct a phase diagram. In the case of Sn-8.8Zn eutectic alloy, the as-cast microstructure was typical lamellar. With addition of 0.25wt.%Y, a large amount of pro-eutectic α phase have been observed and various YZnx intermetallic compounds were expected to successively form during cooling. Hardness of Sn-8.8Zn alloy was not affected by Y-addition and both alloys could be rolled by 90% at room temperature. Keywords—Sn-Zn eutectic alloy, Yttrium, FactSage®, microstructure, mechanical properties.
منابع مشابه
Influence of Ag micro-particle additions on the microstructure, hardness and tensile properties of Sn-9Zn binary eutectic solder alloy
In this study, an addition of Ag micro-particles (8–10 lm) with a content in the range between 0 and 1.5 wt.% to Sn–9Zn eutectic solder, were examined in order to understand the effect of Ag additions as the particulate reinforcement on the microstructural and mechanical properties as well as the thermal behavior of the newly developed composite solders. Here, an approach to prepare a micro-com...
متن کاملStructural and Mechanical Characterization of Austempered Cu - Sn Ductile Iron Alloys
The effect of heat treatment and alloying elements of copper and tin on the microstructure and mechanical properties of austempered ductile cast iron alloys is investigated. The austenitizing temperature of 890°C, the isothermal transformation (austempering) temperatures of 285, 335 and 375°C, and austempering times of 15, 30, 75 and 150 minutes are studied. The alloying elements of copper and ...
متن کاملInvestigation of microstructure and physical properties in nanocomposite solder reinforced with various percent of graphene nanosheets (SAC0307+GNSs)
Development of electronic industries, compression of electronic equipment, and removing lead from electronic circuits for environmental issues, resulted in a significant challenge in design and development of tin-based lead-free solders with physical and mechanical properties similar to old tin-lead alloys. In this regard, the set of Sn-Ag-Cu alloys with eutectic and near eutectic compositions ...
متن کاملInvestigation of microstructure and physical properties in nanocomposite solder reinforced with various percent of graphene nanosheets (SAC0307+GNSs)
Development of electronic industries, compression of electronic equipment, and removing lead from electronic circuits for environmental issues, resulted in a significant challenge in design and development of tin-based lead-free solders with physical and mechanical properties similar to old tin-lead alloys. In this regard, the set of Sn-Ag-Cu alloys with eutectic and near eutectic compositions ...
متن کاملEffects of growth rate on the physical and mechanical properties of Sn-3.7Ag-0.9Zn eutectic alloy
Sn-3.7wt.%Ag-0.9wt.%Zn alloy was directionally solidified upward under different conditions, with different growth rates (V = 3.38 220.12 μm/s) at a constant temperature gradient (G = 4.33 K/mm) and with different temperature gradients (G = 4.33 -12.41 K/mm) at a constant growth rate (V = 11.52 μm/s) by using a Bridgman-type directional solidification furnace. The microstructure was observed to...
متن کامل