Corrosion-Fatigue Crack Growth in Plates: A Model Based on the Paris Law
نویسندگان
چکیده
In this paper, a Paris law-based model is presented whereby crack propagation occurs under cyclic loading in air (fatigue) and in an aggressive environment (corrosion-fatigue) for the case of corner cracks (with a wide range of aspect ratios in the matter of the initial cracks) in finite-thickness plates of 316L austenitic stainless steel subjected to tension, bending, or combined (tension + bending) loading. Results show that the cracks tend during their growth towards a preferential propagation path, exhibiting aspect ratios slightly lower than unity only for the case of very shallow cracks, and diminishing as the crack grows (increasing the relative crack depth)-more intensely in the case of bending than in the case of tension (the mixed loading tension/bending representing an intermediate case). In addition, the crack aspect ratios during fatigue propagation evolution are lower in fatigue (in air) than in corrosion-fatigue (in aggressive environment).
منابع مشابه
Probability Approach for Prediction of Pitting Corrosion Fatigue Life of Custom 450 Steel
In this study, the pitting type of corrosion growth characteristics, fatigue crack initiation and propagation behavior; axial fatigue tests were carried out on precipitation hardened martensitic Custom 450 steel in the air and 3.5wt% NaCl solution. Using the ratio of the depth to the half-width of the pits; (a/c)= 1.5±0.2 the corrosion pit depth growth law was obtained as a function of stress a...
متن کاملModeling of Corrosion-Fatigue Crack Growth Rate Based on Least Square Support Vector Machine Technique
Understanding crack growth behavior in engineering components subjected to cyclic fatigue loadings is necessary for design and maintenance purpose. Fatigue crack growth (FCG) rate strongly depends on the applied loading characteristics in a nonlinear manner, and when the mechanical loadings combine with environmental attacks, this dependency will be more complicated. Since, the experimental inv...
متن کاملFracture mechanics-based life prediction of a riveted lap joint
In this paper, three-dimensional modeling of the fatigue crack growth profiles was performed in a simple riveted lap joint. Simulation results showed that mode I was dominated on the one side of the plates and the crack straightly grew on this side, while the other side of the plates was in a mixed-mode condition and the crack propagation path was not straight on this side. Afterward, the fract...
متن کاملتعیین سرعت رشد خستگی در اتصالات لولهای به وسیله شبکههای عصبی مصنوعی
In order to predict the residual life of offshore platforms and establish efficient schedule for underwater inspection and repair, it is necessary to estimate the fatigue crack growth rate in tubular joints properly. Linear Elastic Fracture Mechanics and Stress Intensity Factor are applicable tools for evaluating growth rate of existing fatigue cracks in offshore tubular joints. In the past sev...
متن کاملAn incremental formulation for the prediction of two-dimensional fatigue crack growth with curved paths
This paper presents a new incremental formulation for predicting the curved growth paths of twodimensional fatigue cracks. The displacement and traction boundary integral equations (BIEs) are employed to calculate responses of a linear elastic cracked body. The Paris law and the principle of local symmetry are adopted for defining the growth rate and direction of a fatigue crack, respectively. ...
متن کامل